RESUMEN
Nowadays, the tremendous progress of nanotechnologies and materials science facilitates the fabrication of universal and multifunctional superhydrophobic surfaces on a large scale. Yet, integrating icephobic and anti-bioadhesive properties in an individual water-repellent functional coating, for addressing the difficulties faced by cryobiologists, aircraft, and seacraft manufacturers, is quite tricky but feasible if using nonpolar soot nanoparticles, whose fragility, however, impedes their industrial applicability. Here, we advance the current state-of-the-art to an extent, permitting the introduction of economically affordable and ultradurable non-wettable soot-based coatings. The deposition of rapeseed oil soot, cyanoacrylate glue and fluorine compounds onto different fabrics confers the latter with superior tolerance to harsh mechanical and thermal interventions [e.g., scratching, blade scraping, liquid nitrogen immersion (T â¼ -196 °C), torsion and water jetting], while in the meantime retaining water repellency and oleophobicity. The as-prepared soot fabrics can stick continuously to the selected host surface and favor the recovery of â¼60% of the initial motility of human spermatozoa subjected to cryopreservation or being detached and utilized as standalone non-wettable membranes. Our invention may be considered as the first fundamental stage of safely (without any health concerns) transferring the soot in reproductive medicine and developing enhanced cryogenic and antibacterial medical devices.
Asunto(s)
Semen , Hollín , Humanos , Masculino , Criopreservación , Interacciones Hidrofóbicas e Hidrofílicas , Espermatozoides , Agua/químicaRESUMEN
Poly(lactic) acid (PLA) film with 2 wt% mixed carbon nanofillers of graphene nanoplates (GNPs) and multiwall carbon nanotubes (MWCNTs) in a weight ratio of 1:1 with impurities of fullerene and carbon black (CB) was produced by layer-to-layer deposition and hot pressing. The release of carbon nanoparticles from the film was studied at varying time-temperature conditions and simulants. Migrants in simulant solvents were examined with laser diffraction analysis and transmission electron microscopy (TEM). Film integrity and the presence of migrants on the film surfaces were visualised by scanning electron microscopy (SEM). The partial dissolution of PLA polymer in the solvents was confirmed by swelling tests and differential scanning calorimetry (DSC). Nanoparticle migrants were not detected in the simulants (at the LOD 0.020 µm of the laser diffraction analysis) after migration testing at 40°C for 10 days. However, high-temperature migration testing at 90°C for 4 h provoked a release of GNPs from the film into ethanol, acetic acid and oil-based food simulants. Short carbon nanotubes were observed rarely to release in the most aggressive acetic acid solvent. Obviously, the enhanced molecular mobility at temperatures above the glass transition and partial dissolution of PLA polymer by the food simulant facilitate the diffusion processes. Moreover, shape, size and concentration of nanoparticles play a significant role. Flexible naked GNPs (lateral size 100-1000 nm) easily migrate when the polymer molecules exhibit enhanced mobility, while fibrous MWCNTs (> 1 µm length) formed entangled networks on the film surfaces as the PLA polymer is partly dissolved, preventing their release into food simulants. The impurities of fullerenes and CB (5-30 nm) were of minor concentration in the polymer, therefore their migration is low or undetectable. The total amount of released migrants is below overall migration limits.