RESUMEN
The addition of CaF2@SiO2 and SiC whiskers to ceramic tools can improve their flexural strength and fracture toughness, reduce surface damage, and improve their cutting performance. The cutting experiments showed that under the same cutting conditions, the surface roughness of the workpiece processed with the Al2O3/TiC/SiC/CaF2@SiO2 (ATSC10) tool was significantly lower than that of the workpiece processed with the Al2O3/TiC/ SiC (ATS) tool. Additionally, the main cutting force and cutting temperature when cutting with the ATSC10 tool were lower by 30 and 31.7%, respectively. These results were attributed to the precipitation of CaF2 from the nanocoated particles during cutting and the formation of a uniform and continuous lubricating film on the surface of the tool. The wear on the front surface of the ATS tool was mainly adhesive, and that on the back tool surface was mainly abrasive. For ATSC10, the main forms of wear on the tool front surface were adhesive and abrasive, whereas the main form of wear on the tool back surface was abrasive with slight adhesive wear. The addition of nano-coated particles and whiskers improved the mechanical properties of the cutting tool while maintaining good cutting performance.
RESUMEN
Aiming at the contradiction between the lubricating performance and mechanical performance of self-lubricating ceramic tools. CaF2@Al(OH)3 particles were prepared by the heterogeneous nucleation method. An Al2O3/Ti(C,N) ceramic tool with CaF2@Al2(OH)3 particles and ZrO2 whiskers was prepared by hot press sintering (frittage). The cutting performances and wear mechanisms of this ceramic tool were investigated. Compared with the Al2O3/Ti(C,N) ceramic tool, the Al2O3/Ti(C,N)/ZrO2/CaF2@Al(OH)3 ceramic tool had lower cutting temperatures and surface roughness. When the cutting speed was increased from 100m/min to 300m/min, a lot of CaF2 was smeared onto the surface of the ceramic tool, and the flank wear of the Al2O3/Ti(C,N)/ZrO2/CaF2@Al(OH)3 ceramic tool was reduced. The main wear mechanisms of the Al2O3/Ti(C,N)/ZrO2/CaF2@Al(OH)3 ceramic tool were adhesive wear and micro-chipping. The formation of solid lubricating film and the improvement of fracture toughness by adding ZrO2 whiskers and CaF2@Al(OH)3 were important factors for the Al2O3/Ti(C,N)/ZrO2/CaF2@Al(OH)3 ceramic tool to have better cutting performances.
RESUMEN
In order to reduce the influence of CaF2 addition on the mechanical properties of self-lubricating ceramic tools, we applied a silicon dioxide (SiO2) coating on calcium fluoride (CaF2) nanoparticles through hydrolysis and condensation reactions using the tetraethoxysilane (TEOS) method. The powder was dried by the azeotropic method, so that it acquired a better dispersibility. The resulting composite powders were characterized using XRD (X-ray diffraction) and TEM (transmission electron microscopy), showing that the surface of CaF2 was coated with a layer of uniform and compact SiO2. SiO2 shells with different thicknesses could be obtained by changing the amount of TEOS added, and the thickness of the SiO2 shells could be controlled between 1.5 and 15 nm. At the same time, a ceramic material containing CaF2 nanoparticles and CaF2@SiO2-coated nanoparticles was prepared. It had the best mechanical properties when CaF2@SiO2-coated nanoparticles were added; its flexural strength, fracture toughness, and hardness were 562 ± 28 MPa, 5.51 ± 0.26 MPa·m1/2, and 15.26 ± 0.16 GPa, respectively. Compared with the ceramic tool containing CaF2 nanoparticles, these mechanical properties were increased by 17.57%, 12.67%, and 4.88%, respectively. The addition of CaF2@SiO2-coated nanoparticles greatly improved the antifriction and wear resistance of the ceramic material, and the antifriction and wear resistance were balanced.