RESUMEN
The preparation of anodic TiO2 nanotube layers has been performed using electrochemical anodization of Ti foil for 4 h at different voltages (from 0 V to 80 V). In addition, a TiO2 thin layer has been also prepared using the sol-gel method. All the photocatalysts have been characterized by XRD, SEM, and DRS to investigate the crystalline phase composition, the surface morphology, and the optical properties, respectively. The performance of the photocatalyst has been assessed in versatile photocatalytic reactions including the reduction of N2O gas and the oxidation of aqueous sulfamethoxazole. Due to their high specific surface area and excellent charge carriers transport, anodic TiO2 nanotube layers have exhibited the highest N2O conversion rate (up to 10% after 22 h) and the highest degradation extent of sulfamethoxazole (about 65% after 4 h) under UVA light. The degradation mechanism of sulfamethoxazole has been investigated by analyzing its transformation products by LC-MS and the predominant role of hydroxyl radicals has been confirmed. Finally, the efficiency of the anodic TiO2 nanotube layer has been tested in real wastewater reaching up to 45% of sulfamethoxazole degradation after 4 h.
Asunto(s)
Nanotubos , Aguas Residuales , Sulfametoxazol/química , Catálisis , Nanotubos/química , Titanio/químicaRESUMEN
In the present work, nanotwin structured TiO2 nanotube (TNT) layers are prepared by the electrochemical anodization technique to form the anatase phase and by surface modification via spin-coating of Ce and V precursors to form Ce-TNT and V-TNT, respectively. The surface and cross-sectional images by SEM revealed that the nanotubes have an average diameter of â¼130 nm and a length of â¼14 µm. In addition, the TEM images revealed the nanotwin structures of the nanotubes, especially the anatase (001) and (112) twin surfaces, that increase the transport of photogenerated charges. The photoinduced degradation of caffeine (CAF) by TNT, Ce-TNT, and V-TNT led to a degradation extent of 16%, 26% and 33%, respectively, whereas it increased to 26%, 38%, and 46% in the presence of H2O2, owing to the involvement of Fenton-based processes (in addition to photocatalysis). The effect of the Fenton-based processes accounts for about 10% of the total degradation extent of CAF. Finally, the mechanism of the photoinduced degradation of CAF was investigated. The main oxidative species were the hydroxyl radicals, and the better efficiency of V-TNT over Ce-TNT and TNT was ascribed to its negative surface, thus improving the interactions with CAF.