The honeybee's comb has inspired the design of engineering honeycomb core that primarily abstract the hexagonal cell shape and exploit its mass minimizing properties to construct lightweight panels. This work explored three additional design features that are part of natural honeybee comb but have not been as well studied as design features of interest in honeycomb design: the radius at the corner of each cell, the coping at the top of the cell walls, and the interface between cell arrays. These features were first characterized in natural honeycomb using optical and X-ray techniques and then incorporated into honeycomb core design and fabricated using an additive manufacturing process. The honeycomb cores were then tested in out-of-plane compression and bending, and since all three design features added mass to the overall structure, all metrics of interest were examined per unit mass to assess performance gains despite these additions. The study concluded that the presence of an interface increases specific flexural modulus in bending, with no significant benefit in out-of-plane compression; coping radius positively impacts specific flexural strength, however, the corner radius has no significant effect in bending and actually is slightly detrimental for out-of-plane compression testing.
RESUMEN
The characterization of additively manufactured cellular materials, such as honeycombs and lattices, is crucial to enabling their implementation in functional parts. One of the characterization methods commonly employed is mechanical testing under compression. This work focuses specifically on the dependence of these tests to the applied strain rate during the test over low strain rate regimes (considered here as 10-6 to 10-1 s-1). The paper is limited to the study of strain the rate dependence of hexagonal honeycomb structures manufactured with four different additive manufacturing processes: one polymer (fused deposition modeling, or material extrusion with ABS), one composite (nylon and continuous carbon fiber extrusion) and two metallic (laser powder bed fusion of Inconel 718 and electron beam melting of Ti6Al4V). The strain rate sensitivities of the effective elastic moduli, and the peak loads for all four processes were compared. Results show significant sensitivity to strain rate in the polymer and composite process for both these metrics, and mild sensitivity for the metallic honeycombs for the peak load. This study has implications for the characterization and modeling of all mechanical cellular materials and makes the case for evaluation and if appropriate, inclusion, of strain rate effects in all cellular material modeling.