RESUMEN
OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.
Asunto(s)
Recubrimiento Dental Adhesivo , Dentina , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Técnica de Perno Muñón , Cementos de Resina , Humanos , Cementos de Resina/química , Recubrimiento Dental Adhesivo/métodos , Dentina/efectos de la radiación , Técnicas In Vitro , Recubrimientos Dentinarios/química , Análisis del Estrés Dental , Propiedades de Superficie , Raíz del Diente/efectos de la radiación , Ultrasonido , Grabado Ácido Dental , Incisivo , Vidrio/químicaRESUMEN
OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.