RESUMEN
A novel hybrid single Li-ion conductor (SLIC) for a Li-ion solid electrolyte was prepared by mixing aluminate complexes-polyethylene glycol (LiAl-PEG) and polyethylene oxide (PEO) for solid-state Li-ion batteries. The LiAl-PEG/PEO blend possesses high thermal stability and electrochemical stability with an oxidation decomposition voltage up to 4.8 V. Notably, this hybrid SLIC exhibits not only excellent Li-ion migration kinetics, but also good ionic conductivity as high as 4.0 × 10-5 and 2.6 × 10-4 S cm-1 at 30 and 100 °C, respectively, which is much higher than previously reported SLICs. Importantly, by the combination of molecular dynamics simulations and experiment measurements, the mechanisms of Li-ion migration across the SLIC (LiAl-PEG), the salt-in-polymer (LiClO4/PEO) and the optimized SLIC (LiAl-PEG/PEO) were systematically investigated for the first time. The new hopping transport mechanism was verified for the SLIC system at the nanoscale. As for the hybrid SLIC, PEO chains enhance the segmental mobility of the ether-chains bonded with Al atoms, improve the ionicity, and provide extra ionic paths for Li transfer, resulting in the optimized Li-ion migration kinetics of LiAl-PEG/PEO.
RESUMEN
A novel type of organic-inorganic hybrid polymer electrolytes with high electrochemical performances around room temperature is formed by hybrid of nanofillers, Y-type oligomer, polyoxyethylene and Li-salt (PBA-Li), of which the Tg and Tm are significantly lowered by blended heterogeneous polyethers and embedded nanofillers with benefit of the dipole modification to achieve the high Li-ion migration due to more free-volume space. The quasi-solid-state Li-ion batteries based on the LiFePO4/15PBA-Li/Li-metal cells present remarkable reversible capacities (133 and 165 mAh g-1 @0.2 C at 30 and 45 °C, respectively), good rate ability and stable cycle performance (141.9 mAh g-1 @0.2 C at 30 °C after 150 cycles).