RESUMEN

Continuous monitoring of greenhouse gases with high spatio-temporal resolution has lately become an urgent task because of tightening environmental restrictions. It may be addressed with an economically efficient solution, based on semiconductor metal oxide gas sensors. In the present work, CO2 detection in the relevant concentration range and ambient conditions was successfully effectuated by fine-particulate La2O3-based materials. Flame spray pyrolysis technique was used for the synthesis of sensitive materials, which were studied with X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), diffuse reflectance infrared Fourier transform spectroscopy (DRIFTs) and low temperature nitrogen adsorption coupled with Brunauer-Emmett-Teller (BET) effective surface area calculation methodology. The obtained materials represent a composite of lanthanum oxide, hydroxide and carbonate phases. The positive correlation has been established between the carbonate content in the as prepared materials and their sensor response towards CO2. Small dimensional planar MEMS micro-hotplates with low energy consumption were used for gas sensor fabrication through inkjet printing. The sensors showed highly selective CO2 detection in the range of 200-6667 ppm in humid air compared with pollutant gases (H2 50 ppm, CH4 100 ppm, NO2 1 ppm, NO 1 ppm, NH3 20 ppm, H2S 1 ppm, SO2 1 ppm), typical for the atmospheric air of urbanized and industrial area.

Asunto(s)

RESUMEN

Field Cycling (FC) 2H nuclear magnetic resonance (NMR) relaxometry was applied to study dynamics in Nafion NR 212 in the temperature range from 300 K to 190 K and water content of λ = 8.2. The sensitive time window of FC was extended up to eight decades using the temperature-frequency superposition principle and master curve. The rotational correlation times obtained from 2H FC NMR coincide with translational correlation times gained from static field 2H NMR diffusometry in the temperature range applied. This fact means that a long-range mass transport in Nafion is coupled to molecular rotations. It is assumed that confined water in Nafion has more ordered oxygen sublattices as compared with bulk water, on a short range is similar to ice. We discuss the possible role of D and L defects, typical for the ordered ice structure and using this concept to describe the processes of self-diffusion of confined water in Nafion, as well as the similarity of temperature and humidity dependence of self-diffusion and proton conductivity.