RESUMEN
Hard anodizing is used to improve the anodic films' mechanical qualities and aluminum alloys' corrosion resistance. Applications for anodic oxide coatings on aluminum alloys include the space environment. In this work, the aluminum alloys 2024-T3 (Al-Cu), 6061-T6 (Al-Mg-Si), and 7075-T6 (Al-Zn) were prepared by hard anodizing electrochemical treatment using citric and sulfur acid baths at different concentrations. The aim of the work is to observe the effect of citric acid on the microstructure of the substrate, the mechanical properties, the corrosion resistance, and the morphology of the hard anodic layers. Hard anodizing was performed on three different aluminum alloys using three citric-sulfuric acid mixtures for 60 min and using current densities of 3.0 and 4.5 A/dm2. Vickers microhardness (HV) measurements and scanning electron microscopy (SEM) were utilized to determine the mechanical characteristics and microstructure of the hard anodizing material, and electrochemical techniques to understand the corrosion kinetics. The result indicates that the aluminum alloy 6061-T6 (Al-Mg-Si) has the maximum hard-coat thickness and hardness. The oxidation of Zn and Mg during the anodizing process found in the 7075-T6 (Al-Zn) alloy promotes oxide formation. Because of the high copper concentration, the oxide layer that forms on the 2024-T6 (Al-Cu) Al alloy has the lowest thickness, hardness, and corrosion resistance. Citric and sulfuric acid solutions can be used to provide hard anodizing in a variety of aluminum alloys that have corrosion resistance and mechanical qualities on par with or better than traditional sulfuric acid anodizing.
RESUMEN
In this work, titanium dioxide scaffolds were synthesized. Titanium isopropoxide (IV) was used as a precursor in its formation, using a polymeric network of galactopyranose as a template. The powder sample obtained was evaluated by scanning tunneling microscopy (STM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) analysis, and thermal gravimetric analysis (TGA-DTA). According to the results, it was found that these scaffolds can be successfully synthesized in solution using the sol-gel method. The synthesized scaffolds have diameters from 50 nm with porosity of approximately 0.3-10 nm. Important parameters, such as pH and the concentration of the metallic precursors, were optimized in this solution. The values of maximum average roughness R(max) and roughness value (Ra) were 0.50 and 1.45, respectively. XRD diffraction analysis shows the formation of crystalline phases in the TiO2 scaffold at 700 °C. The use of biological polymers represents an alternative for the synthesis of new materials at low cost, manipulating the conditions in the production processes and making the proposed system more efficient.
RESUMEN
The aim of this work was to evaluate the corrosion behavior of the AA6061 and AlSi10Mg alloys produced by extruded and additive manufacturing (selective laser melting, SLM). Alloys were immersed in two electrolytes in H2O and 3.5 wt. % NaCl solutions at room temperature and their corrosion behavior was studied by electrochemical noise technique (EN). Three different methods filtered EN signals, and the statistical analysis was employed to obtain Rn, the localization index (LI), Kurtosis, skew, and the potential spectral density analysis (PSD). The Energy Dispersion Plots (EDP) of wavelets method was employed to determine the type of corrosion and the Hilbert-Huang Transform (HHT), analyzing the Hilbert Spectra. The result indicated that the amplitude of the transients in the time series in potential and current is greater in the AlSi10Mg alloy manufactured by additive manufacturing. The amplitude of the transients decreases in both alloys (AA6061 and AlSi10Mg) as time increases.