On the basis of aminoethers of boric acid (AEBA), polyurethane vapor-permeable and pervaporative membranes were obtained. AEBAs, the structure of which is modified by bulk adducts (EM) of diphenylol propane diglycidyl ether and ethanolamine, were studied. It turned out that AEBA exists in the form of clusters, and the use of EM as a result of partial destruction of associative interactions leads to a significant decrease in the size of AEBA-EM particles and their viscosity compared to unmodified AEBA. The introduction of EM into the composition of AEBA leads to a threefold increase in the vapor permeability of polyurethanes obtained on their basis. The observed effect is explained by the fact that a decrease in the size of clusters leads to loosening of their dense packing. Areas of clustering due to associative interactions of hydroxyl groups, together with the hydrophilic nature of polyoxyethylene glycol, create channels through which water molecules can penetrate. The increase in vapor permeability is accompanied by a multiple increase in the permeability coefficients in the pervaporative dehydration of isopropanol.
RESUMEN
Organophosphorus polyurethane ionomers (AEPA-PU) based on aminoethers of ortho-phosphoric acid (AEPA) were obtained and studied as pervaporation membrane materials for separating isopropanol/water mixtures. The regularities of the change in the water vapor permeability of AEPA-PU were also investigated. It has been established that an increase of solute content in the composition of the urethane-forming system and the content of ionogenic groups in AEPA leads to a noticeable increase in the vapor permeability of the resulting film materials. An increase in water vapor permeability values is accompanied by a significant increase in the pervaporation characteristics of AEPU-PU. It was shown that the conditions promoting clustering of phosphate anions cause an increase in the values of the vapor permeability coefficient of AEPA-PU obtained using polyoxypropylene glycol. However, the hydrophobicity of the polypropylene glycol surrounding the clusters makes it difficult for water to move through the polymer matrix. Due to the hydrophilicity of polyoxyethylene glycol, the highest values of water vapor permeability and pervaporation characteristics are achieved for AEPA-PU synthesized using PEG.