RESUMEN

PURPOSE: To evaluate the effect of overglazing and two polishing procedures on flexural strength and quality and quantity of surface roughness of a monolithic lithium disilicate ceramic computer-aided design (CAD) after grinding. MATERIALS AND METHODS: This in vitro study was conducted on 52 partially crystalized bar-shaped specimens (16 × 4 × 1.6 mm) of monolithic lithium disilicate ceramic. The specimens were wet polished with 600-, 800-, and 1200-grit silicon carbide papers for 15 seconds using a grinding/polishing machine at a speed of 300 rpm. Then, the specimens were crystalized and glaze-fired in one step simultaneously and randomly divided into four groups of 13: (I) Glazing group (control); (II) Grinding-glazing group, subjected to grinding with red band finishing diamond bur (46 µm) followed by glazing; (III) Grinding-D+Z group, subjected to grinding and then polishing by coarse, medium, and fine diamond rubber points (D+Z); and (IV) Grinding-OptraFine group, subjected to grinding and then polishing with a two-step diamond rubber polishing system followed by a final polishing step with an OptraFine HP brush and diamond polishing paste. The surface roughness (Ra and Rz) values (µm) were measured by a profilometer, and the mean values were compared using one-way ANOVA and Tamhane's test (post hoc comparison). One specimen of each group was evaluated under a scanning electron microscope (SEM) for surface topography. The three-point flexural strength values of the bars were measured using a universal testing machine at a 0.5 mm/min crosshead speed and recorded. The data were analyzed using one-way ANOVA and Tamhane's test (α = 0.05). RESULTS: Statistically significant differences were noted among the experimental groups for Ra, Rz (p < 0.0001), and flexural strength values (p < 0.009). The lowest Ra and Rz values were found in the grinding-OptraFine group (0.465 ± 0.153), which were significantly lower than those in glazing (p < 0.03) and grinding-glazing (p < 0.001) groups. The Ra and Rz values were not significantly different between the two polishing systems (p = 0.23 and p = 0.25, respectively). The highest flexural strength was found in the glazing group (283.350 ± 49.854 MPa) without significant differences compared to grinding-glazing (p = 0.98) and grinding-OptraFine groups (p = 0.86). The lowest flexural strength was found in grinding-D+Z group (225.070 ± 17.299), which was significantly different from the value in glazing (p < 0.03) and grinding-glazing (p < 0.04) groups. SEM analysis of polished surfaces revealed regular morphology with some striations. CONCLUSIONS: The OptraFine system created smoother and more uniform surfaces in terms of quantity (p < 0.03 for Ra, p < 0.01 for Rz) and quality of roughness compared to glazing. The flexural strength of lithium disilicate ceramic after polishing with the OptraFine system was similar to that after glazing (p = 0.86). Despite similar surface roughness after polishing with the two systems, the D+Z system reduced the flexural strength of ceramic (p < 0.03).

Asunto(s)

Cerámica/química , Pulido Dental/métodos , Porcelana Dental/química , Resistencia Flexional , Compuestos Inorgánicos de Carbono , Diseño Asistido por Computadora , Materiales Dentales/química , Pulido Dental/instrumentación , Restauración Dental Permanente , Diamante , Humanos , Técnicas In Vitro , Ensayo de Materiales , Ajuste Oclusal , Compuestos de Silicona , Estrés Mecánico , Propiedades de Superficie

RESUMEN

INTRODUCTION: As a consequence of root canal preparation, dentinal chips, irrigants and pulp remnants are extruded into preradicular space. This phenomenon may lead to post endodontic flare-ups. The purpose of this study was to compare the amount of extruded debris with four endodontic NiTi engine-driven systems. METHODS AND MATERIALS: Sixty mesiobuccal roots of maxillary molars with 15-30˚ curvature were divided randomly into four groups (n=15). Each group was instrumented up to apical size of 25 using Reciproc, ProTaper Universal, Neolix and Hyflex. Bidistilled water was used as irrigant and extruded debris was collected in pre-weighted Eppendorf tubes. Tubes were stored in incubator for drying the debris. Extruded debris were weighted in electronic microbalance with accuracy of 0.0001 g. The raw data was analyzed with one way analysis of variance (ANOVA) and Tukey's HSD post hoc test. Level of significance was set at 0.05. RESULTS: The debris extrusion with Reciproc files was significantly higher than the other groups (P<0.05). Hyflex significantly extruded less debris than other files (P<0.05). There was no significant difference between ProTaper Universal and Neolix regarding the amount of extruded debris (P=0.98). CONCLUSION: All systems extruded debris during the instrumentation. Reciproc system significantly extruded more debris. Caution should be taken when interpreting the results of this study and applying it to the real clinical situation.