RESUMEN
The incorporation of titanium dioxide nanoparticles into concrete blocks for paving adds photocatalytic functionality to the cementitious matrix, providing self-cleaning and pollutant-degrading properties. However, wear and leaching from these pavements can release potentially toxic compounds into water bodies, affecting aquatic organisms. In this context, this study evaluated the toxicological effects of leachates from photocatalytic concrete containing nano-TiO2 with an average size of 10 nm and anatase crystallinity on Daphnia magna. Acute and chronic toxicity tests on neonates were conducted with two leachate extracts: one from reference concrete and one from photocatalytic concrete (with 9% nano-TiO2 added by mass of cement). In terms of acute toxicity, the reference concrete extract had an EC50 of 104.0 mL/L at 48 h, whereas the concrete with TiO2 had an EC50 of 64.6 mL/L at 48 h. For chronic toxicity, the leachate from reference concrete had a significant effect (p < 0.05) on the size parameter with an LOEC of 4 mL/L, whereas the leachate from concrete with 9% nano-TiO2 did not have significant toxicological effects on any of the analyzed parameters (longevity, size, reproduction, and age of first posture) (LOEC > 6.5 mL/L). Furthermore, FTIR analysis indicated that TiO2 nanoparticles were not detected in the leachates, suggesting efficient anchoring within the cementitious matrix. The results indicate that there was no increase in the chronic toxicity of the leachate from the cementitious matrix when nanoparticles were added at a 9% mass ratio of cement.
RESUMEN
The incorporation of nanomaterials in binders in the paving area has been studied to improve the mechanical behavior of asphalt mixtures. However, asphalt mixture compounds are susceptible to leaching and deposition in the environment. In this context, this research aimed to investigate the toxic effect of two leachate extracts from asphalt mixtures nanomodified with 2% carbon nanotube and 3% organophilic nanoclay, compared to conventional mixture, using Daphnia magna and Landoltia punctata as test organisms. The nanomaterials were characterized to confirm morphology, stability and effective diameter. Extracts were chemically characterized using the Fourier-Transform Infrared Spectroscopy (FTIR) technique, which indicated presence of functional groups of the asphalt binder in greater intensity in the leachate from conventional mixture. Acute toxicity with D. magna indicated EC50,48h of 83.5 ± 6.2 mL/L for leachate extract from conventional mixture, 306.0 ± 87.6 mL/L for leachate extract from mixture with nanoclay and 464.8 ± 32.1 mL/L for leachate extract from mixture with carbon nanotube. No leachate caused significant chronic toxicity. As for L.punctata, concentrations that caused 50% growth inhibition were 127.5 mL/L for the leachate extract from mixture with carbon nanotube, 196.9 mL/L for the leachate extract from mixture with nanoclay and 205 mL/L for the leachate extract from conventional mixture. For these test organisms, there is no evidence of negative impacts directly associated with the use of the present nanomaterials in asphalt mixtures. The incorporation of these nanos may also reduce the acute toxicity of the mixtures.