RESUMEN
In this study, it was aimed to analyze the effects of liposomes on the dyeing of polyacrylonitrile fabrics. For this purpose, firstly liposome synthesis was carried out, and then liposome production was confirmed by Fourier transform infrared spectroscopy analysis. Additionally, zeta potential measurements were carried out to see whether stable structures were formed. Then, a selected basic dye was encapsulated with a liposome and the possibilities of using these capsules as alternative to retarders in the dyeing of polyacrylonitrile fabrics were examined. According to results obtained, it can be said that the 1% solution of synthesized liposomes creates a more stable suspension with a polydispersity index of 0.472 and the average particle size of 165.2 nm. On the other hand, it has been revealed that if 1% liposome is used in dyeing, a kind of retarder effect can be achieved in the dyeing of polyacrylonitrile fabrics. Moreover, it can be said that the decrease in color efficiency, that is, the loss of yield, caused by the use of liposome at the end of dyeing is lower compared to the retarder. This is also a very important issue, because a good retarder is expected to slow down the dye uptake, but not reduce the dye intake too much at the end of the dyeing. Dyeing levelness (%) was found to be 96.1, 97.4, and 97.1 for dyeings without auxiliary, with 1% cationic retarder and with 1% liposome, respectively. Beyond this, no significant difference was observed in terms of fastness of dyeing.
RESUMEN
In this study, guesthost inclusion complexes of silver abietate with ß-cyclodextrin were prepared by kneading and physical mixing techniques, and analyzed via fourier transformed infrared spectroscopy (FTIR) and thermogravimetric analyser (TGA). The 1:1 and 1:2 stoichiometry of the guesthost were prepared. Obtained FTIR and TGA results showed that formation of silver abietate:ß-cyclodextrin (Ag-A:ß-CD) inclusion complexes occurred at a mass ratio of both 1:1 and 1:2. Furthermore, prepared Ag-A:ß-CD (1:2) inclusion complex was doped in Poly(vinyl alcohol) nanofibers during electrospinning process for obtaining nanowebs. The formation of nanowebs were investigated under scanning electron microscope (SEM), X-Ray diffraction (XRD), Fourier transformed infrared spectroscopy (FTIR) and thermogravimetric analyser (TGA). The results confirmed Ag-A:ß-CD inclusion complex containing Poly(vinyl alcohol) (PVA) nanoweb production.