RESUMEN
Ti6Al4V is one of the most lightweight, mechanically resistant, and appropriate for biologically induced corrosion alloys. However, surface properties often must be tuned for fitting into biomedical applications, and therefore, surface modification is of paramount importance to carry on its use. This work compares the interaction between two different cell lines (L929 fibroblasts and osteoblast-like MG63) and medical grade Ti6Al4V after surface modification by plasma nitriding or thin film deposition. We studied the adhesion of these two cell lines, exploring which trends are consistent for cell behavior, correlating with osseointegration and in vivo conditions. Modified surfaces were analyzed through several physicochemical characterization techniques. Plasma nitriding led to a more pronounced increase in surface roughness, a thicker aluminum-free layer, made up of diverse titanium nitride phases, whereas thin film deposition resulted in a single-phase pure titanium nitride layer that leveled the ridged topography. The selective adhesion of osteoblast-like cells over fibroblasts was observed in nitrided samples but not in thin film deposited films, indicating that the competitive cellular behavior is more pronounced in plasma nitrided surfaces. The obtained coatings presented an appropriate performance for its use in biomedical-aimed applications, including the possibility of a higher success rate in osseointegration of implants.