RESUMEN

The rise in the antibiotic resistance of bacteria has increased scientific interest in the study of materials with unique mechanisms of antimicrobial action. This paper presents the results of studies on the antimicrobial activity of carbon materials and textiles decorated with them. A comparative analysis of the bactericidal and fungicidal activities of graphene oxide, electrochemically exfoliated multigraphene, carbon dots, and their combinations was performed. Microbiological studies on reference strains of E. coli, S. aureus, and C. albicans showed that graphene oxide inhibited growth with up to 98% efficiency. Electrochemically exfoliated multigraphene was less effective (up to 40%). This study found no significant antimicrobial activity of carbon dots and the combination of carbon dots with graphene oxide significantly weakened their effectiveness. However, the combination of electrochemically exfoliated multigraphene and carbon dots exhibits a synergistic effect (up to 76%). A study on the antimicrobial activity of decorated cotton textiles demonstrated the effectiveness of antimicrobial textiles with graphene oxide, electrochemically exfoliated multigraphene, and a combination of carbon dots with electrochemically exfoliated multigraphene.

Asunto(s)

Antiinfecciosos , Fibra de Algodón , Grafito , Grafito/química , Grafito/farmacología , Antiinfecciosos/farmacología , Antiinfecciosos/química , Escherichia coli/efectos de los fármacos , Escherichia coli/crecimiento & desarrollo , Candida albicans/efectos de los fármacos , Candida albicans/crecimiento & desarrollo , Carbono/química , Staphylococcus aureus/efectos de los fármacos , Pruebas de Sensibilidad Microbiana , Textiles , Puntos Cuánticos/química

RESUMEN

The rapid development of electric vehicles, unmanned aerial vehicles, and wearable electronic devices has led to great interest in research related to the synthesis of graphene with a high specific surface area for energy applications. However, the problem of graphene synthesis scalability, as well as the lengthy duration and high energy intensity of the activation processes of carbon materials, are significant disadvantages. In this study, a novel reactor was developed for the green, simple, and scalable electrochemical synthesis of graphene oxide with a low oxygen content of 14.1%. The resulting material was activated using the fast joule heating method. The processing of mildly oxidized graphene with a high-energy short electrical pulse (32 ms) made it possible to obtain a graphene-based porous carbon material with a specific surface area of up to 1984.5 m2/g. The increase in the specific surface area was attributed to the rupture of the original graphene flakes into smaller particles due to the explosive release of gaseous products. In addition, joule heating was able to instantly reduce the oxidized graphene and decrease its electrical resistance from >10 MΩ/sq to 20 Ω/sq due to sp2 carbon structure regeneration, as confirmed by Raman spectroscopy. The low energy intensity, simplicity, and use of environment-friendly chemicals rendered the proposed method scalable. The resulting graphene material with a high surface area and conductivity can be used in various energy applications, such as Li-ion batteries and supercapacitors.

RESUMEN

In this study, cotton e-textiles were obtained using two types of graphene oxide. The first type of graphene oxide was synthesized using the Hummers' method. The second type was obtained by the electrochemical exfoliation of graphite in an ammonium salt solution. It was shown that e-textiles based on electrochemically exfoliated graphene have a higher electrical conductivity (2 kΩ/sq) than e-textiles based on graphene oxide obtained by the Hummers' method (585 kΩ/sq). In addition, textiles based on electrochemically exfoliated graphene exhibit better washing and mechanical stress stability. The electrical resistance of the e-textiles increased only 1.86 times after 10 cycles of washing, compared with 48 times for the Hummers' method graphene oxide textiles. The X-ray photoelectron spectra of the two types of graphene oxides showed similarity in their functional compositions after reduction. Studies of individual graphene flakes by atomic force microscopy showed that graphene oxide of the second type had a smaller lateral size. Raman spectroscopy showed a higher degree of sp2 structure regeneration after reduction for the second type of graphene. These properties and the tendency to form agglomerated particles determine the mechanochemical stability and high electrical conductivity of e-textiles based on electrochemically exfoliated graphene.