RESUMEN
In this study, nanocomposite film was fabricated using cellulose nanocrystals (CNCs) as nanofiller in a polymer matrix of polyvinyl alcohol (PVA) and gum tragacanth (GT) via solution casting. CNCs were extracted from sugarcane bagasse using a steam explosion technique followed by acid hydrolysis. Initial analysis of CNCs by transmission electron microscopy (TEM) showed nanosized particles of 104 nm in length and 7 nm in width. Physical and chemical characteristics of neat PVA, PVA/GT, and PVA/GT/CNC films with varying concentrations of CNCs (from 2% to 10%) were analyzed by the scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectrometry, mechanical test, and swelling test. The SEM analysis showed cluster formation of CNCs in the polymer matrix at high concentration. The developed films were transparent. FTIR spectrometry analysis confirmed the chemical functional groups of the various components in the film. The presence of GT and CNCs in the polymer matrix improved the characteristics of films as evident in the prolonged stability for 7 days and increased mechanical properties. The highest elastic modulus of 1526.11 ± 31.86 MPa and tensile strength of 80.39 MPa were recorded in PVA/GT/CNC2 film. The swelling ability, however, decreased from 260% to 230%. Cytotoxicity analysis of the PVA/GT/CNC film showed that it is nontoxic to mouse fibroblast cells L929 with 95% cell viability. Films loaded with betel leaf extract exhibited excellent antibacterial activities against Staphylococcus aureus DMST 8840 and Pseudomonas aeruginosa TISTR 781 with 28.20 ± 0.84 mm and 23.60 ± 0.55 mm inhibition zones, respectively. These results demonstrate that PVA/GT/CNC loaded with the betel leaf extract could act as promising and versatile wound dressings to protect the wound surface from infection and dehydration.
RESUMEN
The goal of this study is to isolate cellulose nanocrystals (CNC) from sugarcane leaves (SCL) and fabricate filter membranes. Filter membranes consisting of the CNC and varying amount graphene oxide (GO) were fabricated using vacuum filtration technique. The α-cellulose content increased from 53.56 ± 0.49 % in untreated SCL to 78.44 ± 0.56 % and 84.99 ± 0.44 % in steam-exploded and bleached fibers, respectively. Atomic force microscopy (AFM) and transmission electron microscope (TEM) of CNC isolated from SCL indicated nanosized particles in the range of 7.3 nm and 150 nm for diameter and length, respectively. Morphologies of the fiber and CNC/GO membranes were determined by scanning electron microscopy (SEM) and crystallinity by X-ray diffraction (XRD) analysis of crystal lattice. The crystallinity index of CNC decreased with the addition of GO into the membranes. The CNC/GO-2 recorded the highest tensile index of 3.001 MPa. The removal efficiency increases with increasing GO content. The highest removal efficiency of 98.08 % was recorded for CNC/GO-2. CNC/GO-2 membrane reduced growth of Escherichia coli to 65 CFU compared to >300 CFU of control sample. SCL is a potential bioresource for isolation of cellulose nanocrystals and fabrication of high-efficiency filter membrane for particulate matter removal and inhibition of bacteria.