RESUMEN

While efficient removal of uremic toxins and accumulated water is pivotal for the well-being of dialysis patients, protein adsorption to the dialyzer membrane reduces the performance of a dialyzer. Hydrophilic membrane modification with polyvinylpyrrolidone (PVP) has been shown to reduce protein adsorption and to stabilize membrane permeability. In this study we compared middle molecule clearance and filtration performance of nine polysulfone-, polyethersulfone-, and cellulose-based dialyzers over time. Protein adsorption was simulated in recirculation experiments, while ß2-microglobulin clearance as well as transmembrane pressure (TMP) and filtrate flow were determined over time. The results of this study showed that ß2-microglobulin clearance (-7.2 mL/min/m2) and filtrate flow (-54.4 mL/min) decreased strongly during the first 30 min and slowly afterwards (-0.7 mL/min/m2 and -6.8 mL/min, respectively, for the next 30 min); the TMP increase (+37.2 mmHg and +8.6 mmHg, respectively) showed comparable kinetics. Across all tested dialyzers, the dialyzer with a hydrophilic modified membrane (FX CorAL) had the highest ß2-microglobulin clearance after protein fouling and the most stable filtration characteristics. In conclusion, hydrophilic membrane modification with PVP stabilizes the removal capacity of middle molecules and filtration performance over time. Such dialyzers may have benefits during hemodiafiltration treatments which aim to achieve high exchange volumes.

RESUMEN

INTRODUCTION: Hydrophilic modification with polyvinylpyrrolidone (PVP) increases the biocompatibility profile of synthetic dialysis membranes. However, PVP may be eluted into the patient's blood, which has been discussed as a possible cause for adverse reactions rarely occurring with synthetic membranes. We investigated the content of PVP and its elution from the blood-side surface from commercially available dialyzers, including the novel FX CorAL, with PVP-enriched and α-tocopherol-stabilized membrane, and link the results to the level of platelet loss during dialysis as a maker of biocompatibility. METHODS: Six synthetic, PVP containing, dialyzers (FX CorAL, FX CorDiax [Fresenius Medical Care]; Polyflux, THERANOVA [Baxter]; ELISIO [Nipro]; xevonta [B. Braun]) were investigated in the present study. The content of PVP on blood-side surface was determined with X-ray photoelectron spectroscopy (XPS). The amount of elutable PVP was measured photometrically after 5 h recirculation. The level of platelet loss was evaluated in an ex vivo recirculation model with human blood. FINDINGS: Highest PVP content on the blood-side surface was found for the polysulfone-based FX CorAL (26.3%), while the polyethersulfone-based THERANOVA (15.6%) had the lowest PVP content. Elution of PVP was highest for the autoclave steam-sterilized THERANOVA (9.1 mg/1.6 m2 dialyzer) and Polyflux (9.0 mg/1.6 m2 dialyzer), while the lowest PVP elution was found for the INLINE steam sterilized FX CorAL and FX CorDiax (<0.5 mg/1.6 m2 dialyzer, for both). Highest platelet loss was found for xevonta (+164.4% compared to the reference) and the lowest for the FX CorAL (-225.2%) among the polysulfone-based dialyzers; among the polyethersulfone-based dialyzers, THERANOVA (+95.5%) had the highest and ELISIO (-52.1%) the lowest platelet loss. DISCUSSION: Polyvinylpyrrolidone content and elution differ between commercially available dialyzers and were found to be linked to the membrane material and sterilization method. The amount of non-eluted PVP on the blood-side surface may be an important determinant for the biocompatibility of dialyzers.

Asunto(s)

RESUMEN

Activation of the complement system may occur during blood-membrane interactions in hemodialysis and contribute to chronic inflammation of patients with end-stage renal disease. Hydrophilic modification with polyvinylpyrrolidone (PVP) has been suggested to increase the biocompatibility profile of dialysis membranes. In the present study we compared the complement activation of synthetic and cellulose-based membranes, including the polysulfone membrane with α-tocopherol-stabilized PVP-enriched inner surface of the novel FX CorAL dialyzer, and linked the results to their physical characteristics. Eight synthetic and cellulose-based dialyzers (FX CorAL, FX CorDiax [Fresenius Medical Care]; Polyflux, THERANOVA [Baxter]; ELISIO, SUREFLUX [Nipro]; xevonta [B. Braun]; FDX [Nikkisio Medical]) were investigated in the present study. Complement activation (C3a, C5a, and sC5b-9) was evaluated in a 3 hours ex vivo recirculation model with human blood. Albumin sieving coefficients were determined over a 4 hours ex vivo recirculation model with human plasma as a surrogate of secondary membrane formation. Zeta potential was measured as an indicator for the surface charge of the membranes. The FX CorAL dialyzer induced the lowest activation of the three complement factors (C3a: -39.4%; C5a: -57.5%; and sC5b-9: -58.9% compared to the reference). Highest complement activation was found for the cellulose-based SUREFLUX (C3a: +154.0%) and the FDX (C5a: +335.0% and sC5b-9: +287.9%) dialyzers. Moreover, the FX CorAL dialyzer had the nearest-to-neutral zeta potential (-2.38 mV) and the lowest albumin sieving coefficient decrease over time. Albumin sieving coefficient decrease was associated with complement activation by the investigated dialyzers. Our present results indicate that the surface modification implemented in the FX CorAL dialyzer reduces the secondary membrane formation and improves the biocompatibility profile. Further clinical studies are needed to investigate whether these observations will result in a lower inflammatory burden of hemodialysis patients.

Asunto(s)