RESUMEN
The effects of filler loading and silane coupling agent on the properties of hydroxyapatite (HAp)-filled high density polyethylene (HDPE) composites have been studied. The (HAp) powder was successfully produced from tilapia scales using the spray drying process utilized to prepare the HDPE/HAp composites. The FTIR peaks for the untreated HDPE/30HAp composite corresponded to the functional groups of HDPE (C-CH3) and -CH2 and HAp (PO4-3 and O-H). The FTIR spectrum for the silane-treated composite showed that the C=O and silanol groups were eliminated, which strongly confirms the chemical interaction between the HAp fillers and the HDPE matrix. The developed composites demonstrated enhanced mechanical performance, and in particular the treated HDPE/30HAp-S composite exhibited superior tensile strength, Young's modulus and flexural modulus of 28.26 MPa, 1272 MPa and 796 MPa, respectively. In vitro cytotoxicity analysis showed that the developed composites were non-toxic and have great potential to be used for biomedical application.
RESUMEN
This work represents a study to investigate the mechanical properties of longitudinal basalt/woven-glass-fiber-reinforced unsaturated polyester-resin hybrid composites. The hybridization of basalt and glass fiber enhanced the mechanical properties of hybrid composites. The unsaturated polyester resin (UP), basalt (B) and glass fibers (GF) were fabricated using the hand lay-up method in six formulations (UP, GF, B7.5/G22.5, B15/G15, B22.5/G7.5 and B) to produce the composites, respectively. This study showed that the addition of basalt to glass-fiber-reinforced unsaturated polyester resin increased its density, tensile and flexural properties. The tensile strength of the B22.5/G7.5 hybrid composites increased by 213.92 MPa compared to neat UP, which was 8.14 MPa. Scanning electron microscopy analysis was used to observe the fracture mode and fiber pullout of the hybrid composites.
RESUMEN
Natural fiber reinforced composites have had a great impact on the development of eco-friendly industrial products for several engineering applications. Sugar palm fiber (SPF) is one of the newly found natural fibers with limited experimental investigation. In the present work, sugar palm fiber was employed as the natural fiber reinforcement. The composites were hot compressed with polyvinyl butyral (PVB) to form the structure of laminated composites and then were subjected to tensile testing and moisture absorption. The maximum modulus and tensile strength of 0.84 MPa and 1.59 MPa were registered for samples PVB 80-S and PVB 70-S, respectively. Subsequently, the latter exhibited the highest tensile strain at a maximum load of 356.91%. The moisture absorption test revealed that the samples exhibited better water resistance as the proportion of PVB increased relative to the proportion of SPF due to the remarkable hydrophobic property of PVB in comparison with that of SPF.