RESUMEN
In this study, a new foaming method, based on physical foaming combined with microwave-induced curing, is proposed in combination with a surface bioactivation to develop scaffold for bone tissue regeneration. In the first step of the process, a stable physical foaming was induced using a surfactant (Pluronic) as blowing agent of a homogeneous blend of Chitosan and polyethylene glycol diacrylate (PEGDA700) solutions. In the second step, the porous structure of the foaming was chemically stabilized by radical polymerization induced by homogeneous heating of the sample in a microwave reactor. In this step, 2,2-azobis[2-(2-imidazolin-2yl)propane]dihydrochloride was used as thermoinitiator (TI). Chitosan and PEGDA were mixed in different blends to investigate the influence of the composition on the final properties of the material. The chemical properties of each sample were evaluated by infrared attenuated total reflectance analysis, before and after curing in order to maximize reaction yield and optimize kinetic parameters (i.e. time curing, microwave power). Absorption capacity, elastic modulus, porosity and morphology of the porous structure were measured for each sample. The stability of materials was evaluated in vitro by degradation test in phosphate-buffered saline. To improve the bioactivity and biological properties of chitosan scaffold, a biomineralization process was used. Biological characterization was carried out with the aim to prove the effect of biomineralization scaffold on human mesenchymal stem cells behaviour. Copyright © 2016 John Wiley & Sons, Ltd.
Asunto(s)
Quitosano/química , Microondas , Polietilenglicoles/química , Andamios del Tejido/química , Materiales Biocompatibles , Huesos/efectos de los fármacos , Calcificación Fisiológica/efectos de los fármacos , Diferenciación Celular , Células Cultivadas , Fuerza Compresiva , Humanos , Ensayo de Materiales , Células Madre Mesenquimatosas/citología , Osteogénesis , Porosidad , Regeneración , Estrés Mecánico , Ingeniería de Tejidos/métodosRESUMEN
The Markâ»Houwinkâ»Sakurada (MHS) equation allows for estimation of rheological properties, if the molecular weight is known along with good understanding of the polymer conformation. The intrinsic viscosity of a polymer solution is related to the polymer molecular weight according to the MHS equation, where the value of the constants is related to the specific solvent and its concentration. However, MHS constants do not account for other characteristics of the polymeric solutions, i.e., Deacetilation Degree (DD) when the solute is chitosan. In this paper, the degradation of chitosan in different acidic environments by thermal treatment is addressed. In particular, two different solutions are investigated (used as solvent acetic or hydrochloric acid) with different concentrations used for the preparation of chitosan solutions. The samples were treated at different temperatures (4, 30, and 80 °C) and time points (3, 6 and 24 h). Rheological, Gel Permeation Chromatography (GPC), Fourier Transform Infrared Spectroscopy (FT-IR), Differential Scanning Calorimetry (DSC) and Thermal Gravimetric Analyses (TGA) were performed in order to assess the degradation rate of the polymer backbones. Measured values of molecular weight have been integrated in the simulation of the batch degradation of chitosan solutions for evaluating MHS coefficients to be compared with their corresponding experimental values. Evaluating the relationship between the different parameters used in the preparation of chitosan solutions (e.g., temperature, time, acid type and concentration), and their contribution to the degradation of chitosan backbone, it is important to have a mathematical frame that could account for phenomena involved in polymer degradation that go beyond the solvent-solute combination. Therefore, the goal of the present work is to propose an integration of MHS coefficients for chitosan solutions that contemplate a deacetylation degree for chitosan systems or a more general substitution degree for polymers in which viscosity depends not only on molecular weight and solvent combinations.
RESUMEN
Physical foaming combined with microwave-induced curing was used in this study to develop an innovative device for bone tissue regeneration. In the first step of the process, a stable physical foaming was induced using a surfactant (i.e. pluronic) as blowing agent of a homogeneous blend of Sodium salt of carboxymethylcellulose (CMCNa) and polyethylene glycol diacrylate (PEGDA700) solution. In the second step, the porous structure of the scaffold was chemically stabilized by radical polymerization induced by a homogeneous rapid heating of the sample in a microwave reactor. In this step 2,2-Azobis[2-(2-imidazolin-2 yl)propane]Dihydrochloride was used as thermoinitiator (TI). CMCNa and PEGDA were mixed with different blends to correlate the properties of final product with the composition. The chemical properties of each sample were evaluated by spectroscopy analysis ATR-IR (before and after curing) in order to maximize reaction yield, and optimize kinetic parameters (i.e. time curing, microwave power). The stability of the materials was evaluated in vitro by degradation test in Phosphate Buffered Saline. Biological analyses were performed to evaluate the effect of scaffold materials on cellular behavior in terms of proliferation and early osteogenic differentiation of human Mesenchymal Stem Cells. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 726-733, 2016.