RESUMEN
Examination of angiosperm primary cell walls by transmission electron microscopy shows that they contain microfibrils that probably consist of cellulose microfibrils surrounded by associated non-cellulosic polysaccharides. Previous studies using solid-state (13)C NMR spectroscopy have shown that the cellulose is all crystalline with crystallites of cross-sectional dimensions of 2-3 nm. However, it is not known if each microfibril contains only one, or more than one crystallite because there is no agreement about the dimensions of the microfibrils. Partially hydrated primary cell walls isolated from onion ( Allium cepa L.) and Arabidopsis thaliana (L.) Heynh. were examined by atomic force microscopy and the microfibril diameters determined. The cell walls of both species contained tightly interwoven microfibrils of uniform diameter: 4.4+/-0.13 nm in the onion and 5.8+/-0.17 nm in A. thaliana. The effect was also examined of extracting the A. thaliana cell walls to remove pectic polysaccharides. The microfibrils in the extracted cell walls of A. thaliana were significantly narrower (3.2+/-0.13 nm) than those in untreated walls. The results are consistent with the microfibrils containing only one cellulose crystallite.
Asunto(s)
Arabidopsis/citología , Pared Celular/ultraestructura , Microfibrillas/ultraestructura , Microscopía de Fuerza Atómica , Cebollas/citología , Arabidopsis/ultraestructura , Cebollas/ultraestructuraRESUMEN
Solid-state CP/MAS 13C NMR spectroscopy was used to determine the effects of three different sequential extraction procedures, used to remove non-cellulosic polysaccharides, on the molecular ordering of cellulose in a cell-wall preparation containing mostly primary cell walls obtained from the leaves of the model dicotyledon, Arabidopsis thaliana. The extractions were 50 mM trans-1,2-diaminocyclohexane N,N,N',N'-tetraacetic acid (CDTA) and 50 mM sodium carbonate (giving Residue 1); 50 mM CDTA, 50 mM sodium carbonate and 1 M KOH (giving Residue 2); and 50 mM CDTA, 50 mM sodium carbonate and 4 M KOH (giving Residue 3). The molecular ordering of cellulose in Residue 1 was similar to that in unextracted walls: the cellulose was almost all crystalline, with 43% of molecules contained in crystallite interiors and similar proportions of the triclinic (I(alpha)) and monoclinic (I(beta)) crystal forms. Residue 2 was partly decrystallized and the remaining crystallites were mostly in the I(beta) form. Residue 3 was a mixture of cellulose II, cellulose I and amorphous cellulose. The presence of signals at 100.0 and 102.3 ppm in the spectra of Residues 1 and 2, but not of unextracted cell walls, suggested that the extractions giving these residues caused some of the non-cellulosic polysaccharides, possibly xyloglucans and galactoglucomannans, to become relatively well ordered, for example through interactions with cellulose crystallite surfaces.