RESUMEN

INTRODUCTION: Axial vascularization represents a mandatory requirement for clinically applied larger scale vascularized bone grafts. The aim of this study was to combine the arteriovenous (AV) loop model in the rat with a critically sized femoral bone defect and to successfully transplant axially vascularized bone constructs into the defect. MATERIALS AND METHODS: In Groups A and C, an AV loop together with a clinically approved hydroxyapatite and beta-tricalcium phosphate (HA/ß-TCP) matrix, mesenchymal stem cells, and recombinant human bone morphogenetic protein 2 were implanted into a newly designed porous titanium chamber with an integrated osteosynthesis plate in the thighs of rats, whereas in Groups B and D, the same matrix composition without AV loop and, in Group E, only the HA/ß-TCP matrix were implanted. After 6 weeks, the constructs were transplanted into a 10 mm femoral defect created in the same leg, in Groups A and C, under preservation of the AV loop pedicle. Group F served as a control group with an empty chamber. Ten days (Groups A and B) and 12 weeks (Groups C-F) after transplantation, the femora together with the constructs were explanted and investigated using computed tomography (CT), micro-CT, X-ray, histology, and real-time polymerase chain reaction (RT-PCR). RESULTS: Ten days after transplantation, Group A showed a maintained vascular supply leading to increased vascularization, cell survival in the scaffold center, and bone generation compared to Group B. After 12 weeks, there was no difference detectable among all groups regarding total vessel number, although Group C, using the AV loop, still showed increased vascularization of the construct center compared to Groups D and E. In Group C, there was still enhanced bone generation detectable compared to the other groups and increased bony fusion rate at the proximal femoral stump. CONCLUSIONS: This study shows the combination of the AV loop model in the rat with a critically sized femoral defect. By maintenance of the vascular supply, the constructs initially showed increased vascularization, leading to increased bone formation and bony fusion in the long term.

Asunto(s)

Trasplante Óseo/métodos , Fémur/lesiones , Supervivencia de Injerto , Trasplantes/irrigación sanguínea , Trasplantes/trasplante , Animales , Proteína Morfogenética Ósea 2/farmacología , Humanos , Masculino , Ratas , Ratas Endogámicas Lew , Proteínas Recombinantes/farmacología

RESUMEN

In addition to good mechanical properties needed for three-dimensional tissue engineering, the combination of alginate dialdehyde, gelatin and nano-scaled bioactive glass (45S5) is supposed to combine excellent cellular adhesion, proliferation and differentiation properties, good biocompatibility and predictable degradation rates. The goal of this study was to evaluate the in vitro and in vivo biocompatibility as a first step on the way to its use as a scaffold in bone tissue engineering. In vitro evaluation showed good cell adherence and proliferation of bone marrow derived mesenchymal stem cells seeded on covalently crosslinked alginate dialdehyde-gelatin (ADA-GEL) hydrogel films with and without 0.1% nano-Bioglass® (nBG). Lactate dehydrogenase (LDH)- and mitochondrial activity significantly increased in both ADA-GEL and ADA-GEL-nBG groups compared to alginate. However, addition of 0.1% nBG seemed to have slight cytotoxic effect compared to ADA-GEL. In vivo implantation did not produce a significant inflammatory reaction, and ongoing degradation could be seen after four weeks. Ongoing vascularization was detected after four weeks. The good biocompatibility encourages future studies using ADA-GEL and nBG for bone tissue engineering application.