Lignin macromolecules are potential precursor materials for producing electrospun nanofibers for composite applications. However, little is known about the effect of lignin type and blend ratios with synthetic polymers. This study analyzed blends of poly(acrylonitrile-co-methyl acrylate) (PAN-MA) with two types of commercially available lignin, low sulfonate (LSL) and alkali, kraft lignin (AL), in DMF solvent. The electrospinning and polymer blend solution conditions were optimized to produce thermally stable, smooth lignin-based nanofibers with total polymer content of up to 20 wt % in solution and a 50/50 blend weight ratio. Microscopy studies revealed that AL blends possess good solubility, miscibility, and dispersibility compared to LSL blends. Despite the lignin content or type, rheological studies demonstrated that PAN-MA concentration in solution dictated the blend's viscosity. Smooth electrospun nanofibers were fabricated using AL depending upon the total polymer content and blend ratio. AL's addition to PAN-MA did not affect the glass transition or degradation temperatures of the nanofibers compared to neat PAN-MA. We confirmed the presence of each lignin type within PAN-MA nanofibers through infrared spectroscopy. PAN-MA/AL nanofibers possessed similar morphological and thermal properties as PAN-MA; thus, these lignin-based nanofibers can replace PAN in future applications, including production of carbon fibers and supercapacitors.
RESUMEN
Globally carbon nanoparticles are increasingly utilized, yet it is not known if these nanoparticles pose a threat to the environment or human health. This investigation examined 'as-prepared', and acid cleaned carbon nanoparticle physicochemical characteristics (by FTIR, TEM, FESEM, UV-VIS and X-ray microanalysis), and whether these characteristics changed following 2.5-7yr exposure to pH neutral saline or fresh water. To determine if these aqueous aged nanotubes were cytotoxic, these nanotubes were incubated with human epithelial monolayers and analyzed for cell viability (vital staining) and ultrastructural nanoparticle binding/localization (TEM, FESEM). The presence of Ni and Y catalyst, was less damaging to cells than CNT lattice surface oxidation. Extended fresh water storage of oxidized CNTs did not reduce surface reactive groups, nor lessen cell membrane destruction or cell death. However storing oxidized CNTs in saline or NOM significantly reduced CNT-induced cell membrane damage and increased cell survival to control levels.