RESUMEN
The purpose of this study was to evaluate the effect of surface roughness and smear layer on the micro-shear bond strength (µSBS) of two self-etching adhesives, Clearfil SE Bond (SE) and Clearfil Tri-S Bond (S3). Flat dentin surfaces were prepared with SiC papers (600-, 180- and 120-grit) and diamond burs (extra fine, medium and coarse). They were further divided into smear-covered and smear-free surfaces and bonded with respective adhesives. µSBS test was performed after water storage at 37ºC for 24 h. Smear layer thickness measurement was evaluated by scanning electron microscope (SEM). Surface roughness was examined by contact stylus profilometer. Smear layer thickness and surface roughness were significantly different among all groups (p<0.05). No difference in µSBS was observed among surface prepared by SiC whereas bur-cut smear layer had negative effect on µSBS, especially for S3. Surface roughness from different surface preparations had no influence on µSBS (p<0.05).
Asunto(s)
Recubrimientos Dentinarios/química , Dentina/ultraestructura , Cementos de Resina/química , Capa de Barro Dentinario , Recubrimiento Dental Adhesivo , Técnicas In Vitro , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Propiedades de SuperficieRESUMEN
The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a newly developed resin cement, ECD-89 (ECD, Tokuyama Dental, Tokyo, Japan) to dentin and to observe the interfacial micromorphology by comparing with two commercial resin cements, Multilink Automix (MA, Ivoclar Vivadent AG, Schaan, Liechtenstein) and Panavia F2.0 (PF, Kuraray Noritake Dental, Tokyo, Japan). Flat dentin surfaces of human third molars were exposed using #600 SiC. After application of primer and cement to the dentin surface, each cement was applied and cured with light (light condition) or without light (dark condition). The teeth were sectioned to obtain beams (1 mm×1 mm) after 24 h of water storage. The mean bond strengths and SDs (MPa) were: ECD: 68.6±14.9, MA: 39.2±18.9, PF: 39.4±18.5 and ECD: 54.5±22.4, MA: 36.7±15.6, PF: 13.4±4.46 when cured in light and dark condition, respectively. In both conditions, ECD-89 showed statistically higher µTBS than the others.
Asunto(s)
Recubrimientos Dentinarios/química , Cementos de Resina/química , Humanos , Técnicas In Vitro , Ensayo de Materiales , Tercer Molar , Compuestos de Organosilicio/química , Propiedades de Superficie , Resistencia a la TracciónRESUMEN
The purpose of this study was to evaluate the effect of remaining dentin thickness (RDT) on the bond strength of current adhesive systems. Third molars were randomly allocated among four groups depending on the adhesive system used: Clearfil SE Bond ONE (SE1), G-Bond PLUS (GB), BeautiBond (BB), and Clearfil Mega Bond (MB). Bonded specimens were stored in water at 37°C for 24 h. Teeth were then sectioned perpendicular to the adhesive interface to produce beams. After measuring RDT of each beam, microtensile bond strength test was carried out using a universal testing machine at a crosshead speed of 1 mm/min. All data were analyzed by linear regression analysis. Bond strengths of one-step self-etch materials used in this study increased with an increase in RDT. In contrast, that of two-step self-etch adhesive system was not affected by RDT.