RESUMEN
The new intermetallic compound Yb7Ni4InGe12 was obtained as large silver needle shaped single crystals from reactive indium flux. Single crystal X-ray diffraction suggests that Yb7Ni4InGe12 crystallizes in the Yb7Co4InGe12 structure type, and tetragonal space group P4/m and lattice constants are a = b = 10.291(2) Å and c = 4.1460(8) Å. The crystal structure of Yb7Ni4InGe12 consists of columnar units of three different types of channels filled with the Yb atoms. The crystal structure of Yb7Ni4InGe12 is closely related to Yb5Ni4Ge10. The effective magnetic moment obtained from the magnetic susceptibility measurements in the temperature range 200-300 K is 3.66µB/Yb suggests mixed/intermediate valence behavior of ytterbium atoms. X-ray absorption near edge spectroscopy (XANES) confirms that Yb7Ni4InGe12 exhibits mixed valence.
RESUMEN
The family of materials RE(4)TGe(8) (RE = Yb, Gd; T = transition metal) exhibits directional zero thermal expansion (ZTE) via a process that is associated with the linking of planar square nets in the third dimension. The Ge square nets in these compounds exhibit commensurate long-range modulations similar to those observed in charge-density-wave compounds. The ZTE is manifested in the plane of the square nets from 10 to 300 K with negligible volume expansion below â¼160 K. The specific atomic arrangement in RE(4)TGe(8) enables a Poisson-like mechanism that allows the structure to contract along one direction as it expands only slightly in the perpendicular direction.
RESUMEN
Yb(3)AuGe(2)In(3) was obtained as large single crystals in high yield from reactions run in liquid indium. Single crystal X-ray diffraction data show that Yb(3)AuGe(2)In(3) is an ordered variant of YbAuIn with lattice constants, a = b = 7.3153(8) Å and c = 4.4210(5) Å, and space group P(6)2m. The parent compound YbAuIn was also studied for comparison. YbAuIn crystallizes in the ZrNiAl structure type, hexagonal, P(6)2m space group with lattice parameters a = b = 7.7127(11) Å and c = 4.0294(8) Å. In Yb(3)AuGe(2)In(3), Ge substitutes for one of the two Au positions in the ternary compound Yb(3)Au(3)In(3). The structure can be described as alternating [Ge(2)In(3)] and [Yb(3)Au] slabs that stack along the c-axis. The magnetic susceptibility data follow a modified Curie-Weiss law. The effective magnetic moment µ(eff) of 0.52 µ(B)/Yb atom was deduced from the Curie constant and Curie-Weiss constant of θ(p) = -1.5 K indicating antiferromagnetic interactions in Yb(3)AuGe(2)In(3). X-ray absorption near edge spectroscopy (XANES) measurements indicate intermediate valency for Yb in both compounds. The metallic nature of both compounds was confirmed by the resistivity measurements. Specific heat data for Yb(3)AuGe(2)In(3) and YbAuIn give an electronic γ term of 31 and 84 mJ/mol·K(2), respectively, suggesting that the ternary analog is a "light" heavy fermion compound.
RESUMEN
The germanide Eu(2)AuGe(3) was obtained as large single crystals in high yield from a reaction of the elements in liquid indium. At room temperature Eu(2)AuGe(3) crystallizes with the Ca(2)AgSi(3) type, space group Fmmm, an ordered variant of the AlB(2) type: a = 857.7(4), b = 1485.5(10), c = 900.2(4) pm. The gold and germanium atoms build up slightly distorted graphite-like layers which consist of Ge(6) and Au(2)Ge(4) hexagons, leading to two different hexagonal-prismatic coordination environments for the europium atoms. Magnetic susceptibility data showed Curie-Weiss law behavior above 50 K and antiferromagnetic ordering at 11 K. The experimentally measured magnetic moment indicates divalent europium. The compound exhibits a distinct magnetic anisotropy based on single crystal measurements and at 5 K it shows a metamagnetic transition at â¼10 kOe. Electrical conductivity measurements show metallic behavior. The structural transition at 130 K observed in the single crystal data was very well supported by the conductivity measurements. (151)Eu Mössbauer spectroscopic data show an isomer shift of -11.24 mm/s at 77 K, supporting the divalent character of europium. In the magnetically ordered regime one observes superposition of two signals with hyperfine fields of 26.0 (89%) and 3.5 (11%) T, respectively, indicating differently ordered domains.
RESUMEN
The Zintl phase, Yb8Ge3Sb5 exhibits a complex lattice response and an abrupt negative thermal expansion below 15 K - subtle structural changes before and after the transition are consistent with temperature-induced electron transfer from (to) Yb 4f bands to (from) Sb 5p and Ge 4p bands.