RESUMEN
The objective of the study was to analyze the influence of coating treatments on sound propagation speeds in thin boards, along the longitudinal and radial directions of resonance wood. The samples studied were thin boards made of spruce and maple wood with dimensions of 240 mm × 80 mm × 4 mm (length × width × thickness) subjected to different coating treatments (oil-based varnish and alcohol varnish) as well as unvarnished samples, exposed to radiation UV, and specimens treated in the saline fog. The test method consisted of evaluating the propagation speeds of Lamb waves applied to thin plates, according to a semicircular test model, so that the results highlighted both the acoustic response in the longitudinal and radial directions as well as the variation in the anisotropy of the samples with the change in the sound propagation direction relative to wood fibers. Based on the statistical analysis, sound propagation speed profiles were obtained in each of the 38 directions analyzed for all wood samples. The results highlighted that the oil-based varnish led to a decrease in the speed of propagation in the radial direction, compared to the alcoholic varnish, whose major effect was in the longitudinal direction, on the spruce wood. On maple wood, increasing the number of varnish layers, regardless of the type of varnish, led to a decrease in the anisotropy ratio between the longitudinal and radial directions.
RESUMEN
TiMoZrTaSi alloys appertain to a new generation of metallic biomaterials, labeled high-entropy alloys, that assure both biocompatibility as well as improved mechanical properties required by further medical applications. This paper presents the use of nondestructive evaluation techniques for new type of alloys, TiMo20Zr7Ta15Six, with x = 0; 0.5; 0.75; 1.0, which were obtained by vacuum melting. In Ti alloys, the addition of Mo improves tensile creep strength, Si improves both the creep and oxidation properties, Zr leads to an α crystalline structure, which increases the mechanical strength and assures a good electrochemical behavior, and Ta is a ß stabilizer sustaining the formation of solid ß-phases and contributes to tensile strength improvement and Young modulus decreasing. The effects of Si content on the mechanical properties of the studied alloys and the effect of the addition of Ta and Zr under the presence of Si on the evolution of crystallographic structure was studied. The influence of composition on fracture behavior and strength was evaluated using X-ray diffraction, resonant ultrasound spectroscopy (RUS) analyses, SEM with energy dispersive X-ray spectroscopy, and acoustic emission (AE) within compression tests. The ß-type TiMo20Zr7Ta15Six alloys had a good compression strength of over 800 MPa, lower Young modulus (69.11-89.03 GPa) and shear modulus (24.70-31.87 GPa), all offering advantages for use in medical applications.