RESUMEN
[Fe-(pyrazine){Pd(CN)4}] (pyrazine = pz) thin films were fabricated using a layer-by-layer assembly approach, a method known to be tunable, versatile, and scalable, since thin films are better-suited for industrial applications. In this study, [Fe-(pz){Pd(CN)4}] powder was synthesized, and the results obtained from a vibrating sample magnetometer verified the presence of an abrupt hysteresis loop with widths of 45 K centered around 300 K, indicating good cooperativity. Super conducting quantum interference device magnetometry results indicated a slow spin transition with temperature but with evidence of hysteresis for thin film samples. X-ray absorption analysis provided further support of the spin crossover behavior but differs from the magnetometry because the spin state transition at the surface differs from the bulk of the thin film. X-ray photoelectron spectroscopy provided some insight into issues with the film deposition process and multiplex fitting was used to further support the claim that the surface of the film is different than the bulk of the film.
RESUMEN
In an effort to reconcile the various interpretations for the cation components of the 2p3/2observed in x-ray photoelectron spectroscopy (XPS) of several spinel oxide materials, the XPS spectra of both spinel alloy nanoparticles and crystalline thin films are compared. We observed that different components of the 2p3/2core level XPS spectra, of these inverse spinel thin films, are distinctly surface and bulk weighted, indicating surface-to-bulk core level shifts in the binding energies. Surface-to-bulk core level shifts in binding energies of Ni and Fe 2p3/2core levels of NiFe2O4thin film are observed in angle-resolved XPS. The ratio between surface-weighted components and bulk-weighted components of the Ni and Fe core levels shows appreciable dependency on photoemission angle, with respect to surface normal. XPS showed that the ferrite nanoparticles NixCo1-xFe2O4(x= 0.2, 0.5, 0.8, 1) resemble the surface of the NiFe2O4thin film. Surface-to-bulk core level shifts are also observed in CoFe2O4and NiCo2O4thin films but not as significantly as in NiFe2O4thin film. Estimates of surface stoichiometry of some spinel oxide nanoparticles and thin films suggested that the apportionment between cationic species present could be farther from expectations for thin films as compared to what is seen with nanoparticles.