RESUMEN
OBJECTIVES: This study aimed to enhance the bond strength between Biodentine™ (BD), a bioactive tricalcium silicate (C3S) based material, and resin composite through various surface treatments. METHODOLOGY: BD samples were immersed in either double distilled water or Hank's Balanced Salt Solution and analyzed using X-ray Diffraction (XRD). Shear bond strength (SBS) evaluations of BD were performed using Prime & Bond™ NT (PNT), Single Bond Universal (SBU), Xeno V (Xeno), and glass ionomer cement (GIC) following various etching durations (0 s/ 15 s/ 30 s/ 60 s with 37.5% phosphoric acid). Two primers, RelyX™ Ceramic Primer (RCP) and Monobond ™ Plus (MBP), were chosen to prime BD for SBS enhancement. Fractography and bonding interfaces were examined with energy dispersive X-ray spectroscopy (EDS)/ scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FTIR). RESULTS: XRD confirmed BD's main compositions as C3S, Ca(OH)2, CaCO3 and ZrO2 after 14 days crystal maturation. Etched BD did not improve SBS. GIC exhibited the lowest SBS (p < 0.05) among all adhesives, regardless of the etching mode (all < 1 MPa). The highest SBS (17.5 ± 3.6 MPa, p < 0.05) was achieved when BD primed with MBP followed by SBU application. FTIR and EDS showed γ-MPTS and10-MDP within the MBP primer interacted with C3S and ZrO2 of BD, achieving enhanced SBS. Most specimens exhibited mixed or cohesive failure modes. Significance BD's subpar mechanical properties and texture may contribute to its poor adhesion to resin composite. Pretreating BD with MBP primer, followed by SBU adhesive is recommended for improving bond strength.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Cementos de Resina/química , Propiedades de Superficie , Materiales Dentales/química , Resinas Compuestas/química , Cementos de Ionómero Vítreo , Resistencia al Corte , Ensayo de MaterialesRESUMEN
Vital pulp therapy (VPT) has gained significant consideration by utilizing the natural healing capacity of the inflamed pulp in healing process. However, the protective pulp capping materials that facilitate this healing process are still under investigation for the successful promotion of dentin-pulp regeneration. Herein, we developed a bioactive and biodegradable pulp capping material (denoted as sCSHA-GFs) by synthesizing inorganic submicron calcium sulfate hemihydrate (sCS)/porous hydroxyapatite (HA) loaded with growth factors (GFs) such as transforming growth factor-beta 1 (TGF-ß1), fibroblast growth factor-2 (FGF-2) and vascular endothelial growth factor (VEGF). Physiochemical characteristics of submicron CSHA-GFs (sCSHA-GFs) cement were determined. Human dental pulp stem cells (hDPSCs) were used for analyzing their biocompatibility and bioactivity for dentin mineralization. To evaluate the efficacy of sCSHA-GFs, we compared it with a commercial material, mineral trioxide aggregate (MTA), the reference standard used clinically on pulp capping. Our results showed that sCSHA-GFs cement presented good biodegradability with dissolution properties for sustained release of calcium (Ca2+) ions and GFs, and facilitated attachment, proliferation, differentiation and migration of hDPSCs. In addition, sCSHA-GFs cement was found to be more effective than MTA at prolonged incubation time in inducing the mRNA expression levels of odontoblastic differentiation markers, dentin sialophosphoprotein (DSPP) and dentin matrix protein (DMP-1), leading to increased mineralization (with calcium deposits) along with increased alkaline phosphatase (ALP) expressions, evident from Alizarin Red S and ALP staining assays. Our findings suggest that sCSHA-GFs cement may act as a suitable material in VPT for dentin-pulp regeneration.