RESUMEN

Objective: The aim of this study was to evaluate the effect of pH and concentration of bleaching agents on the mineral content and surface morphology of human dental enamel for 14 days. Material and Methods: Eighty human central incisors were randomly divided into 8 groups (n=10): G1-7.5% hydrogen peroxide/ pH=9.0; G2­9.5% hydrogen peroxide/pH=9.0; G3- 7.5% hydrogen peroxide/pH=7.0; G4-9.5% hydrogen peroxide/pH=7.0; G5-10% carbamide peroxide/ pH=5.0; G6-16% carbamide peroxide/pH=5.0; G7- 37% phosphoric acid 15s (positive control); G8-no treatment (negative control). The mineral analysis of the bleaching gel collected was assessed by ICP-AES and surface morphology was observed by SEM. Results: Friedman and Dunn's statistical test demonstrated significant differences among the proposed treatments (p0.01). However, the latter groups showed significantly higher values as compared to groups G1, G2, G3 and G4 (p<0.01). Conclusion: Alteration in enamel mineral content may not be influenced by concentration when bleaching agents with the same pH are compared. The most apparent alterations in mineral content and surface morphology may be noted when more acidic products are used. The daily mineral content measurement may not be influenced by repeated applications of bleaching agents. (AU)

Objetivo: Este estudo avaliou o efeito do pH e da concentração de agentes clareadores no conteúdo mineral e na morfologia da superfície do esmalte dental humano durante 14 dias. Material e Métodos: Oitenta incisivos centrais humanos foram aleatoriamente divididos em 8 grupos (n = 10): G1-peróxido de hidrogênio 7.5% /pH = 9.0; G2 - peróxido de hidrogênio 9.5%/pH = 9,0; G3 - peróxido de hidrogênio 7.5%/pH = 7,0; G4-de peróxido de hidrogênio 9.5% / pH = 7,0; G5 - Peróxido de carbamida 10% / pH = 5.0; G6 - peróxido de carbamida 16%/pH = 5.0; G7- ácido fosfórico 37% (controle positivo); G8 - sem tratamento (controle negativo). A análise mineral do gel clareador coletado foi avaliada por ICP-AES e a morfologia da superfície foi observada por MEV. Resultados: Os testes estatísticos de Friedman e Dunn demonstraram diferenças significativas entre os tratamentos propostos (p<0,01). Nenhuma diferença significativa foi encontrada entre os grupos tratados com peróxido de hidrogênio (G1, G2, G3 e G4) ou entre os grupos G5, G6 e G7 (p>0,01), no entanto, os estes grupos apresentaram valores significativamente maiores em relação aos grupos G1, G2, G3 e G4 (p <0,01). Conclusão: Alterações no conteúdo mineral do esmalte não foram influenciadas pela concentração dos agentes clareadores quando os mesmos pH são comparados. As alterações mais significativas no conteúdo mineral e na morfologia da superfície foram notadas quando clareadores mais ácidos foram utilizados. A mensuração diária do conteúdo mineral não foi influenciada por repetidas aplicações de agentes clareadores. (AU)

Asunto(s)

RESUMEN

Bonding plays a major role in dentistry nowadays. Dental adhesives are used in association with composites to solve many restorative issues. However, the wide variety of bonding agents currently available makes it difficult for clinicians to choose the best alternative in terms of material and technique, especially when different clinical situations are considered. Moreover, although bonding agents allow for a more conservative restorative approach, achieving a durable adhesive interface remains a matter of concern, and this mainly due to degradation of the bonding complex in the challenging oral environment. This review aims to present strategies that are being used or those still in development which may help to prevent degradation. It is fundamental that professionals are aware of these strategies to counteract degradation as much as possible. None of them are efficient to completely solve this problem, but they certainly represent reasonable alternatives to increase the lifetime of adhesive restorations.

Asunto(s)

RESUMEN

Abstract Bonding plays a major role in dentistry nowadays. Dental adhesives are used in association with composites to solve many restorative issues. However, the wide variety of bonding agents currently available makes it difficult for clinicians to choose the best alternative in terms of material and technique, especially when different clinical situations are considered. Moreover, although bonding agents allow for a more conservative restorative approach, achieving a durable adhesive interface remains a matter of concern, and this mainly due to degradation of the bonding complex in the challenging oral environment. This review aims to present strategies that are being used or those still in development which may help to prevent degradation. It is fundamental that professionals are aware of these strategies to counteract degradation as much as possible. None of them are efficient to completely solve this problem, but they certainly represent reasonable alternatives to increase the lifetime of adhesive restorations.

Asunto(s)

RESUMEN

OBJECTIVES: To explore the feasibility of a 3D-microleakage protocol for the evaluation of various configurations of adhesive-tooth interfaces. METHODS: Three different kinds of specimens were prepared: (1) a Class-I composite restoration placed without any bonding to maximize gap formation at the interface; (2) a glass-fiber post cemented with a self-adhesive composite cement into a prepared root canal; and (3) inlay MOD composite restorations placed with either a 1-step self-adhesive or a 2-step etch-and-rinse composite cement. After silver-nitrate (AgNO3) infiltration, the specimens were scanned using a Skyscan 1172 X-ray microtomograph (µCT; Skyscan Bruker) at 100kV, 100µA and 7.8-9.5µm resolution. Projection images were reconstructed, after which maximum-intensity projections (MIPs) and 3D-volumetric renderings were produced. For the inlays, an additional conventional stereomicroscopic (SM) microleakage evaluation was accomplished after specimen sectioning. RESULTS: MIPs and 3D-renderings from specimens (1) and (2) revealed strongly varying microleakage patterns along the marginal gap/interface. For the specimens of setup (3), the high radiopacity of the 2-step composite cement hindered evaluation of the MIPs. MIP-microleakage patterns along the enamel margin of the restoration cemented with the 1-step composite cement corresponded well to the stereomicroscopic images. SIGNIFICANCE: The reported µCT-protocol revealed good sensitivity to detect AgNO3 infiltration at the adhesive-tooth interface when considerable microleakage was present. When microleakage was less apparent and spread in a more diffuse pattern, evaluation with µCT was less sensitive compared to stereomicroscopic evaluation.

Asunto(s)

RESUMEN

Introdução: Levando-se em conta que atualmente estão disponíveis aos ortodontistas diferentes materiais para colagem de acessórios ortodônticos e várias marcas comerciais de bráquetes, decidiu-se avaliar, por meio de ensaios mecânicos: 1) A capacidade de retenção, por meio de testes de tração, de bráquetes metálicos das marcas Ormco Orthodontics e Morelli Ortodontia; 2) A resistência adesiva de dois materiais para colagem: sistema adesivo ortodôntico Enlight (Resina Enlight com resina fluída Ortho Solo) e um sistema não específico para ortodontia, formado pela resina composta fotopolimerizável Charisma associada ao adesivo Single Bond; 3) Índice de Remanescente de Adesivo (IRA) presente nas superfícies dentárias após os testes de tração em microscopia ótica. Métodos: Foram utilizados sessenta primeiros pré-molares humanos superiores do lado direito, divididos aleatoriamente em quatro grupos de quinze dentes cada. Os testes de tração foram realizados em máquina de ensaios Instron. Resultados e Conclusão: De acordo com a metodologia empregada e após análise estatística através do programa GMC 2002 (Testes de Kruskal Wallis) e discussão dos resultados obtidos, pôde-se concluir que: os bráquetes Ormco Orthodontics colados com o sistema Enlight apresentaram os maiores valores de resistência à tração, seguidos pelos bráquetes Morelli Ortodontia colados com a mesma resina, bráquetes Ormco Orthodontics colados com a resina Charisma e, por último, bráquetes Morelli Ortodontia colados com resina Charisma. Em relação ao Índice de Remanescente de Adesivo, não houve diferença estatística entre os grupos analisados e a maior parte da resina ficou aderida ao esmalte dentário após as descolagens

Introduction: Taking into account that currently are available to orthodontists different systems for orthodontic bonding of accessories and various trademarks of brackets, we decided to evaluate, through mechanical tests: 1) The bond strength, through tensile tests, of two trademarks of metal brackets: Ormco Orthodontics (Glendora, CA) and Morelli Orthodontics (Sorocaba, SP), 2) The bond strength of two bonding systems: orthodontic adhesive Enlight (Ormco Orthodontics, Glendora, CA) and a system not specific to orthodontics, composed by the composite resin Charisma (Heraeus Kulzer) associated with the adhesive Single Bond (3M ESPE, Monrovia, USA), 3) Adhesive Remnant Index (ARI) in the tooth surfaces after the tensile tests in optical microscope. Methods: Sixty first human upper right premolars were used, all from the right side, which were divided into two groups of thirty teeth, one for each brand of bracket. Each of these has been divided into two groups, one for each composite resin, resulting in four groups of samples: Brackets Ormco Orthodontics (Glendora, CA) associated with Enlight and Ortho Solo (Ormco Orthodontics, Glendora, CA); brackets Ormco Orthodontics (Glendora, CA) associated with Charisma (Heraeus Kulzer) and adhesive Single Bond (3M ESPE); brackets Morelli Orthodontia (Sorocaba, SP) associated with Enlight and Ortho Solo (Ormco Orthodontics, Glendora, CA) and brackets Morelli Orthodontia (Sorocaba, SP) with Charisma (Heraeus Kulzer) and adhesive Single Bond (3M ESPE). The tests were performed in the Instron tensile testing machine. Results and Conclusion: According to the methodology employed and after statistical analysis using the program 2002 GMC (Kruskal Wallis tests) and discussion of the results, we could conclude that the Ormco Orthodontics brackets bonded with Enlight (Ormco Orthodontics) associated with Ortho Solo fluid resin (Ormco Orthodontics) had the highest values of tensile strength, followed by brackets Morelli Orthodontia bonded with the same resin, brackets Ormco Orthodontics bonded with Charisma resin (Heraeus Kulzer) associated with adhesive Single Bond (3M ESPE), and finally, brackets Morelli Orthodontia bonded with Charisma composite resin associated with Single Bond, which submitted the lowest values of tensile. For the Adhesive Remnant Index (ARI), there was no statistical difference between the groups analyzed and most of the composite resin was attached to the tooth enamel after the debonding

Asunto(s)

RESUMEN

The purpose of this study was to evaluate the influence of intrapulpal pressure simulation on the bonding effectiveness of etch & rinse and self-etch adhesives to dentin. Eighty sound human molars were distributed into eight groups, according to the permeability level of each sample, measured by an apparatus to assess hydraulic conductance (Lp). Thus, a similar mean permeability was achieved in each group. Three etch & rinse adhesives (Prime & Bond NT - PB, Single Bond -SB, and Excite--EX) and one self-etch system (Clearfil SE Bond--SE) were employed, varying the presence or absence of an intrapulpal pressure (IPP) simulation of 15 cmH2O. After adhesive and restorative procedures were carried out, the samples were stored in distilled water for 24 hours at 37 degrees C, and taken for tensile bond strength (TBS) testing. Fracture analysis was performed using a light microscope at 40 X magnification. The data, obtained in MPa, were then submitted to the Kruskal-Wallis test ( a = 0.05). The results revealed that the TBS of SB and EX was significantly reduced under IPP simulation, differing from the TBS of PB and SE. Moreover, SE obtained the highest bond strength values in the presence of IPP. It could be concluded that IPP simulation can influence the bond strength of certain adhesive systems to dentin and should be considered when in vitro studies are conducted.

Asunto(s)

RESUMEN

The purpose of this study was to evaluate the influence of intrapulpal pressure simulation on the bonding effectiveness of etch & rinse and self-etch adhesives to dentin. Eighty sound human molars were distributed into eight groups, according to the permeability level of each sample, measured by an apparatus to assess hydraulic conductance (Lp). Thus, a similar mean permeability was achieved in each group. Three etch & rinse adhesives (Prime & Bond NT - PB, Single Bond -SB, and Excite - EX) and one self-etch system (Clearfil SE Bond - SE) were employed, varying the presence or absence of an intrapulpal pressure (IPP) simulation of 15 cmH2O. After adhesive and restorative procedures were carried out, the samples were stored in distilled water for 24 hours at 37°C, and taken for tensile bond strength (TBS) testing. Fracture analysis was performed using a light microscope at 40 X magnification. The data, obtained in MPa, were then submitted to the Kruskal-Wallis test ( a = 0.05). The results revealed that the TBS of SB and EX was significantly reduced under IPP simulation, differing from the TBS of PB and SE. Moreover, SE obtained the highest bond strength values in the presence of IPP. It could be concluded that IPP simulation can influence the bond strength of certain adhesive systems to dentin and should be considered when in vitro studies are conducted.

Asunto(s)

RESUMEN

O Objetivo Deste estudo avaliar UM Foi Influência da simulação de Pressão intrapulpar Sobre a Eficácia da LigAção do etch e enxaguar etch à dentina e auto- adesivos . Oitenta molares Foram divididos em Grupos Humanos Oito , de De De acordo com o grau de permeabilidade De cada amostra , hum Por medido avaliar Aparelho par Uma condutividade hidráulica (Lp ). Assim , a permeabilidade média similar Foi Realizado em grupo CADA. Sistema UM Lavar etch Três e adesivos (Prime & Bond NT - PB, Single Bond -SB , e Excite - EX ) e de self- etch ( Clearfil SE Bond - SE) Foram utilizados , variando A presença OU Ausência de Pressão intrapulpar (IPP ) simulação de 15 cmH2O. DEPOIS DE Adesivo Procedimentos e restaurador Foram realizados , Como amostras armazenadas Por Foram em água destilada 24 horas a 37 º C, e Levado Para a Resistência à tração (TBS) de testes. A análise da Fratura Foi realizada UM Utilizando microscópicos de luz em Uma Ampliação de 40 X . Os Dados, obtidos em MPa, submetidos Foram AO teste de Kruskal -Wallis (a = 0,05). Os resultados revelaram que A TBS de SB e EX Foi significativamente reduzida em simulação IPP, diferindo da TBS de PB e SE. Além disso , SE OS obtidos maiores valores de Resistência de União Na Presença do IPP. realizados Concluiu- se que Uma simulação IPP PoDE influenciar Uma Resistência de União de Sistemas adesivos à dentina e determinado considerados devem Ser QUANDO estudos in vitro , São Paulo (

Asunto(s)

RESUMEN

A atual tendência ao desenvolvimento de uma odontologia minimamente invasiva tem sido responsável pela introdução de instrumentos e técnicas alternativas de preparo cavitário. Porém, tais tecnologias deveriam não somente preencher os requisitos de uma odontologia conservadora, mas também preparar as paredes da cavidade para o tratamento restaurador adesivo subseqüente. Assim, o objetivo deste estudo foi testar a hipótese nula de que: 1) tanto técnicas convencionais quanto técnicas alternativas de preparo cavitário são capazes de produzir um substrato dentinário receptivo à adesão de sistemas autocondicionantes; e 2) A efetividade adesiva de sistemas autocondicionantes não é influenciada pela interposição da camada de esfregaço. Cem molares humanos íntegros foram aleatoriamente divididos em 20 grupos de acordo com o adesivo e a técnica ou instrumento utilizado. Superfícies planas de dentina média oclusal foram preparadas com instrumento rotatório diamantado convencional (IR); fratura; instrumento rotatório CVD (IRCVD); instrumento ultra-sônico CVD (IUCVD); e laser de Er,Cr:YSGG .Um adesivo condicione-e-lave (Optibond FL/OB) e três autocondicionantes (Adper Prompt L-Pop/AP, Clearfil SE Bond/SE e Clearfil S3 Bond/S3) foram empregados. Os espécimes foram construídos com o compósito Z100/3M ESPE. A resist6encia adesiva foi determinada por meio de teste de microtração após 24 h de estocagem em água a 37oC. Amostras adicionais foram processadas para análise em MEV quanto às características morfológicas apresentas após o preparo das superfícies dentinárias em cada caso. O teste de Kruskal-Wallis (p<0,05) determinou que os grupos preparados com IRCVD, IUCVD e laser apresentaram menores valores de resistência adesiva quando comparados aos grupos controle (IR e fratura). Além disso, os adesivos de menor acidez (SE e S3) foram mais eficientes quando aplicados em dentina fraturada. Concluiu-se que o uso de ...

Asunto(s)

RESUMEN

Introdução: Neste trabalho, estudou-se a força de união da resina composta com diferentes materiais estéticos indiretos. Método: Para tanto, foram estabelecidos 10 grupos constituídos por 10 amostras cada um: Grupo 1 (fargis), 2 (Cesead II), 3 (Solidex) e 4 (Artglass), todas resinas laboratoriais jateadas com Al203 de 501/4m, condicionadas com H3(P0)4 a 37% por 1 minuto e cobertas com silano (Monobond-S); Grupos 5 (D'sign), 6 (Noritake) e 7 (Heraceram), de porcelanas feldspáticas jateadas com Al203' condicionadas com HF a 10% por 4 minutos e cobertas com silano; e Grupos 8 (Cergogold), 9 (Empress) e 10 (Empress 2), de porcelanas injetáveis jateadas com Al203 condicionadas com HF por 2 minutos (G8), 1 minuto (G9) ou 20 segundos (G10) e cobertas com silano. Após aplicação do adesivo Excite, as amostras foram preparadas para teste de tração com a resina composta Inten-S, sendo então armazenadas em água destilada a 37°C por 48h previamente ao ensaio mecânico. Resultados: Os dados obtidos foram submetidos ao teste ANOVA de um critério e teste de Tukey (p<0,05), observando-se as seguintes médias em MPa: 27,31 :t 1.23 (G1); 23,78:t 2.88 (G2); 22,62:t 3.38 (G3); 28,77 :t 2.65 (G4); 28,96 :t 2.01 (G5); 36,45 :t 0.83 (G6); 26,77 :t 7.20 (G7); 26,25 :t 1.39 (G8); 34,96 :t 4.17 (G9);29,23 :t 3.16 (G 10). Conclusão: Conclui-se que a classificação dos materiais em termos de resistência adesiva foi determinada pelas marcas comerciais estudadas, sendo que as porcelanas Noritake e Empress atingiram os maiores valores de resistência adesiva.

Introduction: This study evaluated the bond strength of composite resin for several indirect aesthetic materiaIs. Method: Ten groups consisting of 10 specimens each were formed and classified as follows: Groups 1 (fargis), 2 (Cesead II), 3 (Solidex) and 4 (Artglass), consisted of laboratory resins that were sandblasted with Al203 (50µm), etched with 37% phosphoric acid for 1 minute and silanized (Monobond-S); Groups 5 (D'sign), 6 (Noritake) and 7 (Heraceram), composed of feldspathic porcelains sandblasted with Al203 (50µm), etched with 10% hydrofluoric acid for 4 minutes and silanized; and Groups 8 (Cergogold), 9 (Empress) and 10 (Empress 2), consisted of pressable ceramics that were sandblasted with Al2O3 (50µm), etched with 10% hydrofluoric acid for the following periods: 2 minutes (G8), 1 minute (G9) and 20 seconds (G 10) and silanized. After bonding (Excite) and restorative (Inten-S) procedures, the samples were stored in distilled water at 37°C for 48h and submitted to tensile strength testing. Result: The obtained data were statistically analyzed by one way ANOVA and Tuckey tests, and the following means (MPa) were observed: 27.31 :t 1.23 (G1); 23.78 :t 2.88 (G2); 22.62 :t 3.38 (G3); 28.77 :t 2.65 (G4); 28.96 :t 2.01 (G5); 36.45 :t 0.83 (G6); 26.77 :t 7.20 (G7); 26.25 :t 1.39 (G8); 34.96 :t 4.17 (G9); 29.23 :t 3.16 (G 10). Conclusion: It was found that differences in trademarks should be taken into account when ranking materiaIs with respect to bond strengths. The ceramic materiaIs Noritake and Empress attained the highest bond strength values.

Asunto(s)

Asunto(s)

Asunto(s)

RESUMEN

O controle de infecçäo cruzada em consultórios odontológicos inclui cuidados especiais com as seringas tríplices. Os autores pesquisaram a intensidade de contaminaçäo pela microbiota bucal, de pontas de seringas tríplices usadas no atendimento a pacientes de Dentística Restauradora. Cinqüenta pontas descartáveis (Riskcontrol, Injecta Prod. Odontológicos) foram avaliadas: 10, imediatamente após abertura da embalagem; 30, após o uso em pacientes; e 10, após o uso e a desinfecçäo com álcool etílico 70 por cento P?V, friccionado por um minuto. Em câmara de fluxo laminar, as pontas foram "roladas" sobre a superfície de Tryptic Soy Agar, suplementado com 5 por cento de sangue desfibrinado de carneiro. Após 96 horas de incubaçäo anaeróbia, foi feita avaliaçäo da quantidade de unidades formadoras de colônias (ufc) desenvolvidas. Confirmando a informaçäo do fabricante, as pontas estavam estéreis quando retiradas da embalagem. Em todas as pontas usadas em pacientes, observou-se um número incontável de ufc (maior que 300), revelando intensa contaminaçäo. Nas pontas usadas e desinfetadas com álcool etílico 70 por cento P/V, verificou-se apreciável reduçäo na contagem de colônias (1 a 100 ufc), mas incompatível com a segurança biológica. Os resultados sugerem, como condiçäo ideal, o uso de pontas descartáveis nas seringas tríplices