RESUMEN
In this work, the cell line SW620-GFP has been used in a complete magnetic hyperthermia assay, from the preparation of the ferrofluid with folate-coated iron oxide nanoparticles to in vivo experiments. The physical and chemical characterization of the nanoparticles evidenced their superparamagnetic behaviour, an average diameter of 12 ± 4 nm, a 2 nm coat thickness, and a high-power loss density. The main innovation of the work is the exclusive capability of viable SW620-GFP cells to emit fluorescence, enabling fast analysis of both, cell viability in vitro with an epifluorescence microscope and tumour size and shape in vivo in a non-invasive manner using the iBox technology. Moreover, with this imaging technique, it was possible to demonstrate the successful tumour size reduction in mice applying magnetic hyperthermia three times a week over 3 weeks.
RESUMEN
An exhaustive characterization of the physicochemical properties of gum arabic (GA)-coated Fe3O4 magnetic nanoparticles was conducted in this work. These nanoparticles were obtained via the in-situ coprecipitation method (a fast single-step method) in two GA:Fe ratios, 10:1 and 20:1, respectively. Several experimental techniques were applied in the characterization process, all of them described below. Using Transmission Electron Microcopy images, they were shown to have spherical-like morphology with 11 nm diameter. The Fourier Transform Infrared spectra confirmed the attachment of the GA on the surface of the magnetic nanoparticles (MNPs), providing good colloidal stability from pH 7 to 8. The thickness of the coatings (1.7 nm and 1.1 nm) was determined using thermogravimetric measurements. A high specific absorption rate and superparamagnetic properties were determined using alternant and static magnetic fields, respectively. The GA-coated MNPs were non-cytotoxic, according to tests on HT-29 human intestine cells. Additionally, HT-29 cells were exposed to magnetic fluid hyperthermia at 530 kHz, and the induction of cell death by the magnetic field, due to the heating of GA-coated MNP, was observed.