The focus of this study was the development of a second generation of fiber lasers internally cooled by anti-Stokes fluorescence. The laser consisted of a length of a single-mode fiber spliced to fiber Bragg gratings to form the optical resonator. The fiber was single-moded at the pump (1040â nm) and signal (1064â nm) wavelengths. Its core was heavily doped with Yb, in the initial form of CaF2 nanoparticles, and co-doped with Al to reduce quenching and improve the cooling efficiency. After optimizing the fiber length (4.1â m) and output-coupler reflectivity (3.3%), the fiber laser exhibited a threshold of 160â mW, an optical efficiency of 56.8%, and a radiation-balanced output power (no net heat generation) of 192â mW. On all three metrics, this performance is significantly better than the only previously reported radiation-balanced fiber laser, which is even more meaningful given that the small size of the single-mode fiber core (7.8-µm diameter). At the maximum output power (â¼2â W), the average fiber temperature was still barely above room temperature (428â mK). This work demonstrates that with anti-Stokes pumping, it is possible to induce significant gain and energy storage in a small-core Yb-doped fiber while keeping the fiber cool.
RESUMEN
The first observation of cooling by anti-Stokes pumping in nanoparticle-doped silica fibers is reported. Four Yb-doped fibers fabricated using conventional modified chemical vapor deposition (MCVD) techniques were evaluated, namely, an aluminosilicate fiber and three fibers in which the Yb ions were encapsulated in CaF2, SrF2, or BaF2 nanoparticles. The nanoparticles, which oxidize during preform processing, provide a modified chemical environment for the Yb3+ ions that is beneficial to cooling. When pumped at the near-optimum cooling wavelength of 1040â nm at atmospheric pressure, the fibers experienced a maximum measured temperature drop of 20.5 mK (aluminosilicate fiber), 26.2 mK (CaF2 fiber), and 16.7 mK (SrF2 fiber). The BaF2 fiber did not cool but warmed slightly. The three fibers that cooled had a cooling efficiency comparable to that of the best previously reported Yb-doped silica fiber that cooled. Data analysis shows that this efficiency is explained by the fibers' high critical quenching concentration and low residual absorptive loss (linked to sub-ppm OH contamination). This study demonstrates the large untapped potential of nanoparticle doping in the current search for silicate compositions that produce optimum anti-Stokes cooling.