RESUMEN

OBJECTIVE: (1) to determine the effects of the silver diamine fluoride (SDF) and sodium fluoride (NaF) in demineralized dentin exposed to an acid challenge by pH-cycling, (2) to evaluate the remineralizing capacity of SDF/NaF products based on the physicochemical and mechanical properties of the treated dentin surfaces. METHODOLOGY: In total, 57 human molars were evaluated in different stages of the experimental period: sound dentin - negative control (Stage 1), demineralized dentin - positive control (Stage 2), and dentin treated with SDF/NaF products + pH-c (Stage 3). Several commercial products were used for the SDF treatment: Saforide, RivaStar, and Cariestop. The mineral composition and crystalline and morphological characteristics of the dentin samples from each experimental stage were evaluated by infrared spectroscopy (ATR-FTIR), X-ray diffraction, and electron microscopy (SEM-EDX) analytical techniques. Moreover, the mechanical response of the samples was analyzed by means of the three-point bending test. Statistics were estimated for ATR-FTIR variables by Wilcoxon test, while the mechanical data analyses were performed using Kruskal-Wallis and Mann Whitney U tests. RESULTS: Regarding the chemical composition, we observed a higher mineral/organic content in the SDF/NaF treated dentin + pH-c groups (Stage 3) than in the positive control groups (Saforide p=0.03; Cariestop p=0.008; RivaStar p=0.013; NaF p=0.04). The XRD results showed that the crystallite size of hydroxyapatite increased in the SDF/NaF treated dentin + pH-c groups (between +63% in RivaStar to +108% in Saforide), regarding the positive control. SEM images showed that after application of the SDF/NaF products a crystalline precipitate formed on the dentin surface and partially filled the dentin tubules. The flexural strength (MPa) values were higher in the dentin treated with SDF/NaF + pH-c (Stage 3) compared to the positive control groups (Saforide p=0.002; Cariestop p=0.04; RivaStar p=0.04; NaF p=0.02). CONCLUSIONS: The application of SDF/NaF affected the physicochemical and mechanical properties of demineralized dentin. According to the results, the use of SFD/NaF had a remineralizing effect on the dentin surface even under acid challenge.

Asunto(s)

Dentina , Fluoruros Tópicos , Humanos , Fluoruros Tópicos/farmacología , Fluoruros Tópicos/química , Fluoruro de Sodio/farmacología , Durapatita/farmacología , Concentración de Iones de Hidrógeno

RESUMEN

Abstract Objective (1) to determine the effects of the silver diamine fluoride (SDF) and sodium fluoride (NaF) in demineralized dentin exposed to an acid challenge by pH-cycling, (2) to evaluate the remineralizing capacity of SDF/NaF products based on the physicochemical and mechanical properties of the treated dentin surfaces. Methodology In total, 57 human molars were evaluated in different stages of the experimental period: sound dentin - negative control (Stage 1), demineralized dentin - positive control (Stage 2), and dentin treated with SDF/NaF products + pH-c (Stage 3). Several commercial products were used for the SDF treatment: Saforide, RivaStar, and Cariestop. The mineral composition and crystalline and morphological characteristics of the dentin samples from each experimental stage were evaluated by infrared spectroscopy (ATR-FTIR), X-ray diffraction, and electron microscopy (SEM-EDX) analytical techniques. Moreover, the mechanical response of the samples was analyzed by means of the three-point bending test. Statistics were estimated for ATR-FTIR variables by Wilcoxon test, while the mechanical data analyses were performed using Kruskal-Wallis and Mann Whitney U tests. Results Regarding the chemical composition, we observed a higher mineral/organic content in the SDF/NaF treated dentin + pH-c groups (Stage 3) than in the positive control groups (Saforide p=0.03; Cariestop p=0.008; RivaStar p=0.013; NaF p=0.04). The XRD results showed that the crystallite size of hydroxyapatite increased in the SDF/NaF treated dentin + pH-c groups (between +63% in RivaStar to +108% in Saforide), regarding the positive control. SEM images showed that after application of the SDF/NaF products a crystalline precipitate formed on the dentin surface and partially filled the dentin tubules. The flexural strength (MPa) values were higher in the dentin treated with SDF/NaF + pH-c (Stage 3) compared to the positive control groups (Saforide p=0.002; Cariestop p=0.04; RivaStar p=0.04; NaF p=0.02). Conclusions The application of SDF/NaF affected the physicochemical and mechanical properties of demineralized dentin. According to the results, the use of SFD/NaF had a remineralizing effect on the dentin surface even under acid challenge.

RESUMEN

Children with hemophilia (A or B) are at risk for bleeding episodes, which rank from mild mucosal/soft tissues bleeding to life-threatening hemorrhages. This report describes the dental/medical management provided to an 8.10-year-old patient suffering from uncontrolled bleeding after a surgical procedure to expose both permanent upper central incisors, in which hemophilia was a pure incidental finding. Additionally, diverse precautions to be considered during the dental clinical treatment of hemophilic children are discussed.