RESUMEN
The objective of this work was to evaluate the application of candeuba wax solid lipid nanoparticles (SLN) and xanthan gum (XG) as coatings on guava, and their effect on the fruit's physicochemical and nutritional parameters, complementing a previous publication carried out by Zambrano-Zaragoza et al. (2013). The concentrations of SLN were selected according to those reported as the most (65g/L) and least (75g/L) efficient in post-harvest life preservation, and were compared to a coating of XG and untreated control samples. According to results, the submicron-sized systems used in the coatings with a particle size range of 267-344nm, a polydispersity index <0.2, and zeta potential of -22.8 to -30mV remained stable during 8weeks of storage. The best results were from the fruits coated with 65g/L of SLN and stored at 10°C, as they showed the lowest O2 and CO2 respiration rates and, consequently, less weight loss. They also had the best retention of ascorbic acid and total phenol content, with less change in fruit color compared to the control guava and those coated only with XG. These findings indicate that this batch continued their natural maturation process, but at a slower rate than the other samples. The firmness was affected by the activity of the enzyme pectin methylesterase, but results show that the 65g/L coating was efficient in maintaining fruit texture. In contrast, the 75g/L coating produced epoxy in the fruit, causing physiological damage. Finally, the guava coated with XG only had a maturation rate similar to that of the control fruit.