RESUMEN
A fiber-based single-walled carbon nanotube (SWCNT) thin-film-transistor (TFT) has been proposed. We designed complementary SWCNT TFT circuit based on SPICE simulations, with device parameters extracted from the fabricated fiber-based SWCNT TFTs, such as threshold voltage, contact resistance, and off-/gate-leakage current. We fabricated the SWCNTs CMOS inverter circuits using the selective passivation and n-doping processes on a fiber substrate. By comparing the simulation and experimental results, we could enhance the circuit's performance by tuning the threshold voltage between p-type and n-type TFTs, reducing the source/drain contact resistance and off current level, and maintaining a low output capacitance of the TFTs. Importantly, it was found that the voltage gain, output swing range, and frequency response of the fiber-based inverter circuits can be dramatically improved.
RESUMEN
In this paper, we demonstrate high-performance and hysteresis-free solution-processed indium-gallium-zinc oxide (IGZO) thin-film transistors (TFTs) and high-frequency-operating seven-stage ring oscillators using a low-temperature photochemically activated Al2O3/ZrO2 bilayer gate dielectric. It was found that the IGZO TFTs with single-layer gate dielectrics such as Al2O3, ZrO2, or sodium-doped Al2O3 exhibited large hysteresis, low field-effect mobility, or unstable device operation owing to the interfacial/bulk trap states, insufficient band offset, or a substantial number of mobile ions present in the gate dielectric layer, respectively. To resolve these issues and to explain the underlying physical mechanisms, a series of electrical analyses for various single- and bilayer gate dielectrics was carried out. It is shown that compared to single-layer gate dielectrics, the Al2O3/ZrO2 gate dielectric exhibited a high dielectric constant of 8.53, low leakage current density (â¼10-9 A cm-2 at 1 MV cm-1), and stable operation at high frequencies. Using the photochemically activated Al2O3/ZrO2 gate dielectric, the seven-stage ring oscillators operating at an oscillation frequency of â¼334 kHz with a propagation delay of <216 ns per stage were successfully demonstrated on a polymeric substrate.
RESUMEN
Although transparent conducting oxides (TCOs) have played a key role in a wide range of solid-state electronics from conventional optoelectronics to emerging electronic systems, the processing temperature and conductivity of solution-processed materials seem to be far exceeding the thermal limitations of soft materials and insufficient for high-perfomance large-area systems, respectively. Here, we report a strategy to form highly conductive and scalable solution-processed oxide materials and their successful translation into large-area electronic applications, which is enabled by photoassisted postfunctionalization at low temperature. The low-temperature fabrication of indium-tin-oxide (ITO) thin films was achieved by using photoignited combustion synthesis combined with photoassisted reduction process under hydrogen atmosphere. It was noteworthy that the photochemically activated hydrogens on ITO surface could be triggered to facilitate highly crystalline oxygen deficient structure allowing significant increase of carrier concentration and mobility through film microstructure modifications. The low-temperature postfunctionalized ITO films demonstrated conductivity of >1607 S/cm and sheet resistance of <104 Ω/â¡ under the process temperature of less than 300 °C, which are comparable to those of vacuum-deposited and high-temperature annealed ITO films. Based on the photoassisted postfunctionalization route, all-solution-processed transparent metal-oxide thin-film-transistors and large-area integrated circuits with the ITO bus lines were demonstrated, showing field-effect mobilities of >6.5 cm2 V-1 s-1 with relatively good operational stability and oscillation frequency of more than 1 MHz in 7-stage ring oscillators, respectively.
RESUMEN
The realization of large-area electronics with full integration of 1D thread-like devices may open up a new era for ultraflexible and human adaptable electronic systems because of their potential advantages in demonstrating scalable complex circuitry by a simply integrated weaving technology. More importantly, the thread-like fiber electronic devices can be achieved using a simple reel-to-reel process, which is strongly required for low-cost and scalable manufacturing technology. Here, high-performance reel-processed complementary metal-oxide-semiconductor (CMOS) integrated circuits are reported on 1D fiber substrates by using selectively chemical-doped single-walled carbon nanotube (SWCNT) transistors. With the introduction of selective n-type doping and a nonrelief photochemical patterning process, p- and n-type SWCNT transistors are successfully implemented on cylindrical fiber substrates under air ambient, enabling high-performance and reliable thread-like CMOS inverter circuits. In addition, it is noteworthy that the optimized reel-coating process can facilitate improvement in the arrangement of SWCNTs, building uniformly well-aligned SWCNT channels, and enhancement of the electrical performance of the devices. The p- and n-type SWCNT transistors exhibit field-effect mobility of 4.03 and 2.15 cm2 V-1 s-1 , respectively, with relatively narrow distribution. Moreover, the SWCNT CMOS inverter circuits demonstrate a gain of 6.76 and relatively good dynamic operation at a supply voltage of 5.0 V.