RESUMEN

This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): GI-VM7 + 10% Whiteness, G2-VM7 + 16% Whiteness, G3-VM13 + 10% and G4-VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37 degrees C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann-Whitney tests (p < 0.05). The microhardness values before exposure were: g1-433 (57); g2-486 (22); g3-509 (28); g4-518 (24), and after exposure: G1-349 (32); G2-496 (95); G3-519 (38); G4-502 (81). G2 exhibited a higher and significant difference than GI in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.

Asunto(s)

RESUMEN

This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% and G4- VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37°C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann- Whitney tests (p<0.05). The microhardness values before exposure were: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), and after exposure: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exhibited a higher and significant difference than G1 in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.

Este estudo examinou o efeito do agente clareador peroxido de carbamida a 10% e a 16% na microdureza superficial de ceramicas feldspaticas micro-particuladas (VM7 e VM13, Vita Zahnfabrik). Quarenta corpos-de-prova (8 mm de diametro, 2 mm de espessura) foram divididos em quatro grupos (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% e G4- VM13 + 16% Whiteness. Os agentes clareadores foram aplicados por 8 horas durante 15 dias e os cp foram armazenados em agua destilada a 37°C. A dureza Vickers (HV) de cada cp foi determinada. Os dados foram analisados pelos testes de Wilcoxon e Mann-Whitney (p<0.05). Os valores da dureza antes da exposicao ao agente clareador foram: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), e depois da exposicao: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exibiu diferenca significante e microdureza maior comparado ao G1 nos grupos da VM7 e o efeito da concentracao do clareador foi significante, apresentados atraves dos testes Mann-Whitney. Para VM13, ambos testes, Wilcoxon e Mann-Whitney, nao apresentaram diferenca significante. Quando o peroxido de carbamida a 10% foi avaliado, a microdureza da ceramica VM7 foi afetada, e nao houve diferenca na microdureza entre as ceramicas VM7 e VM13 quando o peroxido de carbamida a 16% foi utilizado.

Asunto(s)