RESUMEN
Blend nanofibers composed of synthetic and natural polymers with carbon nanomaterial, have a great potential for bone tissue engineering. In this study, the electrospun nanocomposite scaffolds based on polyhydroxybutyrate(PHB)-Starch-multiwalled carbon nanotubes (MWCNTs) were fabricated with different concentrations of MWCNTs including 0.5, 0.75 and 1 wt%. The synthesized scaffolds were characterized in terms of morphology, porosity, thermal and mechanical properties, biodegradation, bioactivity, and cell behavior. The effect of the developed structures on MG63 cells was determined by real-time PCR quantification of collagen type I, osteocalcin, osteopontin and osteonectin genes. Our results showed that the scaffold containing 1 wt% MWCNTs presented the lowest fiber diameter (124 ± 44 nm) with a porosity percentage above 80 % and the highest tensile strength (24.37 ± 0.22 MPa). The addition of MWCNTs has a positive effect on surface roughness and hydrophilicity. The formation of calcium phosphate sediments on the surface of the scaffolds after immersion in SBF is observed by SEM and verified by EDS and XRD analysis.MG63 cells were well cultured on the scaffold containing MWCNTs and presented more cell viability, ALP secretion, calcium deposition and gene expression compared to the scaffolds without MWCNTs. The PHB-starch-1wt.%MWCNTs scaffold can be considerable for studies of supplemental bone tissue engineering applications.
Asunto(s)
Nanotubos de Carbono , Ingeniería de Tejidos , Ingeniería de Tejidos/métodos , Nanotubos de Carbono/química , Andamios del Tejido/química , Almidón , Poliésteres/químicaRESUMEN
Efficient design for bone tissue engineering requires an understanding of the appropriate selection of biomimetic natural or synthetic materials and scalable fabrication technologies. In this research, poly (3-hydroxybutyrate) (PHB) and starch (5-15 wt%) as biological macromolecules were used to fabricate novel biomimetic scaffolds by electrospinning method. SEM results of electrospun scaffolds revealed bead-free nanofibers and three-dimensional homogenous structures with highly interconnected pores. Results of FTIR and Raman demonstrated that there were hydrogen bonds between the two polymers. The tensile strength of scaffolds was significantly improved by adding starch up to 10 wt%, from 3.05 to 15.54 MPa. In vitro degradation and hydrophilicity of the scaffolds were improved with the presence of starch. The viability and proliferation of MG-63 cells and alkaline phosphatase (ALP) activity were remarkably increased in the PHB-starch scaffolds compared to the PHB and control samples. The mineralization and calcium deposition of MG-63 cells were confirmed by alizarin red staining. It is concluded that PHB/starch electrospun scaffold could be a good candidate for bone tissue engineering applications.