RESUMEN

The hybrid composite sample based on Prosopis Juliflora (PJ) bark and ramie fibre with different length, weight percentage, and curing temperature were created for the first time in this work. Totally, 120 hybrid composite samples were tested in this study. There were five different fibre lengths: 10 mm, 15 mm, 20 mm, 25 mm, and 30 mm, weight percentages 10 %, 20 %, 30 %, 40 %, and 50 %, and different curing temperatures 80 °C, 90 °C, 100 °C, 110 °C, and 120 °C used to produce the hybrid composite samples. Due to the cross-linking ability with the epoxy matrix, the hybrid composite specimen shows high resistance up to 98 Shore D hardness. The high polarity of the epoxy matrix and the hydrogen bond strengthening effect, increased the composite sample flexural strength by 12 %. The curing temperature of 100 °C, 20 mm fibre length, and 30 % of the hybrid composite sample achieved the highest tensile strength (28.76 MPa), flexural strength (46.54 MPa), impact strength (4.5 J), and hardness strength properties (98 shore D). Thermo gravimetric analysis (TGA) revealed the composite samples initial decomposition temperature (Ti) at 98 °C, maximum decomposition temperature (Tmax) at 320 °C, and the final decomposition temperature (Tf) at 466 °C.