RESUMEN
PURPOSE: To evaluate different polishing methods' effects on the color stability of recent resin composites. METHODS: 160 samples for color stability evaluation and 40 samples for the degree of conversion evaluation were prepared with four different resin composites [Harmonize (H), Filtek Universal (F), Omnichroma (O), Essentia Universal (E)] and light cured. For color stability evaluation, samples prepared from each resin composite were divided into four groups: three polishing procedures and a control group. The ΔE00 was calculated between initial, and after immersion in coffee solution for 12 days. The degree of conversion was evaluated with Fourier Transform Infrared Spectroscopy. The statistical analysis of ΔE00 values was made with the two-way ANOVA, Tukey HSD, and Tamhane's T2 tests. One-way ANOVA and Tukey HSD tests were used to compare the degree of conversion values (P< 0.05). RESULTS: In all composite groups, mylar (control) groups had the highest ΔE00, and no differences between other polishing procedures. According to the polishing procedures, Omnichroma showed the highest ΔE00 values (on mylar groups O vs F, P< 0.001; O vs H, P< 0.001; O vs E, P< 0.001). There was a significant difference between the composite groups in terms of the degree of monomer conversion (P< 0.05). Omnichroma showed, significantly, the highest discoloration. CLINICAL SIGNIFICANCE: Different polishing procedures showed effective performance on current composite surfaces. Omnichroma resin composite showed higher color change than composites with similar properties.