Recently, transition metal dichalcogenides (TMDCs) have attracted great interest due to their unique electronic and optical properties. Chemical vapor deposition (CVD) has been regarded as the most promising method for the synthesis of large-area TMDCs with high reproducibility. Having similar hexagonal crystal structures with many TMDCs, c-plane sapphire is commonly used as a growth substrate in CVD. However, few studies have been reported on the influence of the sapphire substrate on the growth behavior and physical properties of TMDCs. In this work, we demonstrate that higher strain is induced in epitaxially grown WS2 grains via van der Waals interactions with sapphire as compared with misaligned WS2 grains. In addition, this strain was found to enhance overlayer deposition on monolayer WS2, while multilayer growth was not observed in non-epitaxial WS2. Photoluminescence (PL) of the epitaxially grown WS2 grains was reduced, reflecting the effective van der Waals interaction with sapphire. Moreover, low-temperature PL measurements revealed strong influence of the c-plane sapphire surface on the optical properties of WS2. Density functional theory (DFT) calculation supports that the aligned WS2 grains are more strongly bound to the sapphire surface, as compared with misaligned WS2. Our work offers a new insight into the understanding of the influence of the substrate on the CVD-grown TMDC materials.
RESUMEN
Aligned growth of transition metal dichalcogenides and related two-dimensional (2D) materials is essential for the synthesis of high-quality 2D films due to effective stitching of merging grains. Here, we demonstrate the controlled growth of highly aligned molybdenum disulfide (MoS2) on c-plane sapphire with two distinct orientations, which are highly controlled by tuning sulfur concentration. We found that the size of the aligned MoS2 grains is smaller and their photoluminescence is weaker as compared with those of the randomly oriented grains, signifying enhanced MoS2-substrate interaction in the aligned grains. This interaction induces strain in the aligned MoS2, which can be recognized from their high susceptibility to air oxidation. The surface-mediated MoS2 growth on sapphire was further developed to the rational synthesis of an in-plane MoS2-graphene heterostructure connected with the predefined orientation. The in-plane epitaxy was observed by low-energy electron microscopy. Transmission electron microscopy and scanning transmission electron microscopy suggest the alignment of a zigzag edge of MoS2 parallel to a zigzag edge of the neighboring graphene. Moreover, better electrical contact to MoS2 was obtained by the monolayer graphene compared with a conventional metal electrode. Our findings deepen the understanding of the chemical vapor deposition growth of 2D materials and also contribute to the tailored synthesis as well as applications of advanced 2D heterostructures.