RESUMEN
Emerging dye pollution from textile industrial effluents is becoming more challenging for researchers worldwide. The contamination of water by dye effluents affects the living organisms in an ecosystem. Methylene blue (MB) and malachite green (MG) are soluble dyes with a high colour intensity even at low concentration and are hazardous to living organisms. The adsorption method is used in most wastewater plants for the removal of organic pollutants as it is cost-effective, has a high adsorption capacity, and good mechanical stabilities. In this study, a composite adsorbent was prepared by impregnating iron modified silica (FMS) onto polyurethane (PU) foam to produce an iron modified silica/polyurethane (FMS/PU) composite. The composite adsorbent was utilised in batch adsorption of the cationic dyes MB and MG. The effect of adsorption parameters such as the adsorbent load, pH, initial dye concentration, and contact time were discussed. Adsorption kinetics and isotherm were implemented to understand the adsorption mechanism for both dyes. It was found that the adsorption of MB and MG followed the pseudo-second order model. The Langmuir model showed a better fit than the Freundlich model for the adsorption of MB and MG, indicating that the adsorption occurred via the monolayer adsorption system. The maximum adsorption capacity of the FMS/PU obtained for MB was 31.7 mg/g, while for MG, it was 34.3 mg/g. The thermodynamic study revealed that the adsorption of MB and MG were exothermic and spontaneous at room temperature. In addition, the regeneration of FMS/PU was conducted to investigate the composite efficiency in adsorbing dyes for several cycles. The results showed that the FMS/PU composite could be regenerated up to four times when the regeneration efficiency dropped drastically to less than 20.0%. The impregnation of FMS onto PU foam also minimised the adsorbent loss into the environment.
RESUMEN
This paper describes the preparation, characterisation, and potential application of flexible palm oil-based polyurethane foam (PUF) as a support for iron-silica (Fe-Si) adsorbent. Fe-Si/polyurethane composite (Fe-Si/PUC) was prepared by impregnating Fe-Si adsorbent onto the surface of PUF by using a novel immersion-drying method. Morphological analysis of Fe-Si/PUC proved that Fe-Si was successfully impregnated onto the surface of PUF. Compression test and thermogravimetric analysis were carried out to determine the flexibility and thermal stability of Fe-Si/PUC, respectively. The Fe-Si/PUC removed 90.0% of 10 ppm methylene blue (MB) from aqueous solution in 60 min. The reusability study showed that Fe-Si/PUC removed 55.9% of MB on the seventh cycle. Hence, the synthesis of Fe-Si/PUC opens up a new path of implementing palm oil-based PUF to assist in the recovery of an adsorbent for environmental clean-up. The mechanism of physical interaction during the impregnation of Fe-Si adsorbent onto PUF was proposed in this paper.