RESUMEN
Non-woven jute (NWJ) produced from carpet industry waste was oxidized by H2O2 or alkali-treated by NaOH and compared with water-washed samples. Changes in the structure of the NWJ, tracked by X-ray diffraction (XRD), showed that both chemical treatments disrupt hydrogen bond networks between cellulose Iß chains of the NWJ fibers. Thereafter, nano-carbon nitride (nCN) was impregnated, using a layer-by-layer technique, onto water-washed jute samples (nCN-Jw), NaOH-treated samples (nCN-Ja) and-H2O2 treated samples (nCN-Jo). Analysis of the Fourier transform infrared spectroscopy (FTIR) spectra of the impregnated samples revealed that nCN anchors to the water-washed NWJ surface through hemicellulose and secondary hydroxyl groups of the cellulose. In the case of chemically treated samples, nCN is preferentially bonded to the hydroxymethyl groups of cellulose. The stability and reusability of prepared nCN-jute (nCN-J) samples were assessed by tracking the photocatalytic degradation of Acid Orange 7 (AO7) dye under simulated solar light irradiation. Results from up to ten consecutive photocatalytic cycles demonstrated varying degrees of effectiveness across different samples. nCN-Jo and nCN-Ja samples exhibited declining effectiveness over cycles, attributed to bond instability between nCN and jute. In contrast, the nCN-Jw sample consistently maintained high degradation rates over ten cycles, with a dye removal percentage constantly above 90%.
RESUMEN
The aim of this work was to study the efficiency of Fe- and N-doped titania suspensions in the photocatalytic degradation of the herbicides RS-2-(4-chloro-o-tolyloxy)propionic acid (mecoprop, MCPP), (4-chloro-2-methylphenoxy)acetic acid (MCPA), and 3,6-dichloropyridine-2-carboxylic acid (clopyralid, CP) under the visible light (lambda > or = 400 nm) irradiation. The obtained results were compared with those of the corresponding undoped TiO(2) (rutile/anatase) and of the most frequently used TiO(2) Degussa P25. Computational modeling procedures were used to optimize geometry and molecular electrostatic potentials of MCPP, MCPA and CP and discuss the obtained results. The results indicate that the efficiency of photocatalytic degradation is greatly influenced by the molecular structure of the compound. Lowering of the band gap of titanium dioxide by doping is not always favorable for increasing photocatalytic efficiency of degradation.
Asunto(s)
Herbicidas/química , Herbicidas/efectos de la radiación , Titanio/química , Titanio/efectos de la radiación , Catálisis , Simulación por Computador , Hierro/química , Luz , Microscopía Electrónica de Rastreo , Modelos Estadísticos , Nitrógeno/química , Fotoquímica , Espectrofotometría Ultravioleta , Espectroscopía Infrarroja por Transformada de Fourier , Suspensiones , Agua , Difracción de Rayos XRESUMEN
Titanium dioxide nanopowders doped with different amounts of Fe ions were prepared by coprecipitation method. Obtained materials were characterized by structural (XRD), morphological (TEM and SEM), optical (UV/vis reflection and photoluminescence, and Raman), and analytical techniques (XPS and ICP-OES). XRD analysis revealed rutile crystalline phase for doped and undoped titanium dioxide obtained in the same manner. Diameter of the particles was 5-7 nm. The presence of iron ions was confirmed by XPS and ICP-OES. Doping process moved absorption threshold of TiO(2) into visible spectrum range. Photocatalytic activity was also checked. Doped nanopowders showed normal and up-converted photoluminescence.
RESUMEN
In this study, nitrogen-doped titanium dioxide (TiO2) powders were synthesized in two ways: by heating of titanium hydroxide with urea and by direct hydrolysis of titanium tetraisopropoxide (TTIP) with ammonium hydroxide. The samples were characterized by structural (XRD), analytical (XPS), optical (UV/Vis absorption/reflection and Raman spectroscopy) and morphological (SEM, TEM) techniques. The characterization suggested that the doped materials have anatase crystalline form without any detectable peaks that correspond to dopants. The absorption threshold of titanium dioxide was moved in the visible range of optical spectrum from 3.2 eV to 2.20 eV. Particle sizes of synthesized powders were obtained from XRD measurements and from TEM data ranging from 6-20 nm. XPS and Raman spectroscopy were used for detection of nitrogen in doped samples.
RESUMEN
Nonaqueous reactions between titanium(IV) chloride and alcohols (benzyl alcohol or n-butanol) were used for the synthesis of anatase TiO2 particles, while rutile TiO2 particles were synthesized in aqueous media by acidic hydrolysis of titanium(IV) chloride. The X-ray diffraction measurements proved the exclusive presence of either the anatase or the rutile phase in prepared samples. The photoluminescence of both kinds of particles (anatase and rutile) with several well-resolved peaks extending in the visible spectral region was observed, and the quantum yield at room temperature was found to be 0.25%. Photon energy up-conversion from colloidal anatase and rutile TiO2 particles was observed at low excitation intensities. The energy of up-converted photoluminescence spans the range of emission of normal photoluminescence. The explanation of photon energy up-conversion involves mid-gap energy levels originating from oxygen vacancies.